ASTM A327-91(2006)
Standard Test Methods for Impact Testing of Cast Irons
4 стр.
Заменен
Электронный (pdf)Печатное издание
84.24 $ (включая НДС 20%)
Разработчик:
Зарубежные/ASTM
ICS:
77.140.80 Iron and steel castings / Чугунные и стальные отливки
Сборник (ASTM):
01.02 Ferrous Castings; Ferroalloys / Стальное литье, Ферросплавы
Тематика:
Ferroalloys, Castings
Описание
Реферат

This test method for impact testing covers the details of apparatus, test specimens and procedures for cast iron, including gray iron, white iron, malleable iron, ductile iron, and austempered ductile iron, but not including chilled rolls or rolls with white iron skins. The gray and white irons shall be subjected to round bar, single-blow Charpy impact test using a pendulum-type impact machine. Characterization of the fracture toughness of any cast iron should be based upon testing at least three specimens. Either the standard notched or unnotched Charpy impact test shall be employed in testing of malleable or ductile irons. Both types of charpy bars have been designated to characterize the fracture toughness of irons.

Область применения

1.1 These test methods for impact testing cover the details of apparatus, test specimens and procedures for cast iron, including gray iron, white iron, malleable iron, ductile iron, and austempered ductile iron, but not including chilled rolls or rolls with white iron skins.

1.2 The values stated in inch-pound units are to be regarded as the standard. A companion standard, A 327M, lists values in SI units.

This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

1.3 The Charpy-type impact test shall be employed for testing gray and white irons.

1.4 Either the standard notched or unnotched Charpy impact test shall be employed in testing of malleable or ductile irons. Selection of the type bar is dependent upon the specific material to be evaluated as defined in Section .

1.5 Both types of charpy bars have been designated to characterize the fracture toughness of irons. The unnotched Charpy bar, when tested, will produce substantially higher energy values than the notch bar type. The unnotched bar is therefore specified for testing irons that have low fracture toughness characteristics.