ASTM A508/A508M-05b(2010)
Standard Specification for Quenched and Tempered Vacuum-Treated Carbon and Alloy Steel Forgings for Pressure Vessels
8 стр.
Заменен
Печатное изданиеЭлектронный (pdf)
96.72 $ (включая НДС 20%)
Разработчик:
Зарубежные/ASTM
ICS:
77.140.30 Steels for pressure purposes / Стали для работы под давлением
Сборник (ASTM):
01.05 Steel--Bars, Forgings, Bearing, Chain, Tool / Сталь - Прутья, Поковки и Заготовки, Балки
Тематика:
Steel--Structural, Tubes, Plate, Coated
Описание
Реферат

This specification covers quenched and tempered vacuum-treated carbon and alloy steel forgings for pressure vessels, such as those used in reactor systems, specifically, vessel closures, shells, flanges, tube sheets, rings, heads, and similar parts. Steels shall be manufactured by basic electric-furnace process except when secondary ladle refining or remelting process is employed, and shall be vacuum treated prior to or during the pouring of the ingot. Materials shall also go through preliminary heat treatment and quenching for mechanical properties. Heat and product analyses shall be executed to evaluate the conformance of the forgings with specified chemical requirements. Tension and Charpy impact tests shall also be performed to examine the conformance of steel specimens with the following mechanical properties: tensile strength, yield strength, elongation, and reduction of area. Nondestructive inspection procedures, such as magnetic particle examination, and longitudinal wave and angle beam ultrasonic examination, shall also be carried out. Repair welding may be permitted at the option of the purchaser.

Область применения

1.1 This specification covers quenched and tempered vacuum-treated carbon and alloy steel forgings for pressure vessels such as those used in reactor systems. Specifically, it covers forgings for vessel closures, shells, flanges, tube sheets, rings, heads, and similar parts.

1.2 All grades are considered weldable under proper conditions. Welding technique is of fundamental importance, and it is presupposed that welding procedure and inspection will be in accordance with approved methods for the grade of material used.

1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.

1.4 Unless the order specifies the applicable M specification designation, the material shall be furnished to the inch-pound units.

Note 1—Grades 1 and 1A are composed of different chemistries but have the same mechanical requirements.

Ключевые слова:
chromium-molybdenum steel; nickel-chromium-molybdenum alloy steels; pressure vessel service; quenched and tempered steels; steel forgingsalloy; steel forgings carbon; vacuum-treated steels; Vacuum treated steel forgings--specifications; Alloy steel forgings--specifications; Carbon steel forgings--specifications; Chromium-molybdenum steel--specifications; Nickel-chromium-molybdenum alloys--specifications; Nuclear applications/materials--steel (specifications); Pressure vessel steel forgings--specifications; Quenched and tempered steels (specifications)