ASTM A542/A542M-99(2004)e1
Standard Specification for Pressure Vessel Plates, Alloy Steel, Quenched-and-Tempered, Chromium-Molybdenum, and Chromium-Molybdenum-Vanadium
5 стр.
Заменен
Печатное изданиеЭлектронный (pdf)
96.72 $ (включая НДС 20%)
Разработчик:
Зарубежные/ASTM
ICS:
77.140.30 Steels for pressure purposes / Стали для работы под давлением
Сборник (ASTM):
01.04 Steel--Structural, Reinforcing, Pressure Vessel, Railway / Сталь - Конструкционная, арматурная, для сосудов под давлением, рельсовая
Тематика:
Steel--Structural, Tubes, Plate, Coated
Описание
Реферат

This specification covers pressure vessel plates, alloy steel, quenched-and-tempered, chromium-molybdenum, and chromium-molybdenum-vanadium. As a steel making practice, the steel shall be killed and shall conform to specified fine austenitic grain size requirements. Plate types A, B, C, D, and E shall be heat treated by heating to a suitable austenitizing temperature, holding for a sufficient period of time to attain uniform temperature throughout the thickness, and quenching in a suitable liquid medium by spraying or immersion. The steel shall conform to the required chemical compositions. The required mechanical properties that include tension test requirements and notch toughness requirements are presented in details.

Область применения

1.1 This specification covers two types of 21/4 Cr-1 Mo and three types of Cr-Mo-V alloy steel plates for use in the quenched-and-tempered condition, intended for the fabrication of welded pressure vessels and components.

1.2 Material under this specification is available in five types, designated "A," "B," "C,"" D," and "E." Type B is identical to Type A except for restrictive limits for carbon, phosphorus, sulfur, and nickel. The material is also available in five classes having the following strength levels. Type E is available only as Class 4 and 4a.

ClassMinimum Tensile Strength, ksi [MPa]
1 105 [725]
2 115 [795]
3 95 [655]
4 and 4a 85 [585]

1.3 The maximum thickness of plates is limited only by the capacity of the chemical composition to meet the specified mechanical property requirements.

1.4 The minimum thickness of plates is limited to 3/16 in. [5 mm].

1.5 The material is intended to be suitable for fusion welding. Welding technique is of fundamental importance and it is presupposed that welding procedures will be in accordance with approved methods.

1.6 The values stated in either inch-pound units or SI units are to be regarded separately as standard. Within the text, the SI units are shown in brackets. The values stated in each system are not exact equivalents, therefore, each system must be used independently of the other. Combining values from the two systems may result in nonconformance with this specification.

Ключевые слова:
Steel plate-chromium alloy; plates-Cr-Mo/Cr-Mo-V alloy steel, quenched/temperred (for pressure; vessels)