This specification covers the standard requirements for semi-processed cold-rolled magnetic lamination quality steels. These steels shall be made by the basic-oxygen or electric-furnace method and shall be processed by hot rolling, pickling, cold rolling, annealing, and temper rolling. Magnetic lamination steels shall have low-carbon contents and may have manganese, phosphorus, silicon, and aluminum additions to enhance punchability and to improve magnetic characteristics by increasing the electrical resistivity. There are no fixed chemical requirements for these steels only the requirement to meet the specified magnetic properties. These steels must be heat treated by the user to develop the specified magnetic properties. This specification covered steels with thicknesses of 0.0185 in. ( 0.47 mm), 0.022 in. (0.56 mm), 0.025 in. (0.64 mm), 0.028 in. (0.71 mm) and 0.031 in. (0.79 mm). For a given thickness there are three or more core loss types distinguished by maximum allowable core loss after a specified quality development anneal. Magnetic testing shall be done after the specified quality development anneal and shall use the Epstein test method. Magnetic testing shall be done at a test frequency of 60 Hz and a maximum flux density of 15 kG (1.5 T). Test methods to determine the magnetic and mechanical properties are listed. Other typical magnetic and physical properties are listed for reference.
Область применения1.1 This specification covers cold-rolled carbon sheet steel used for magnetic applications. These products, commonly called “cold-rolled magnetic lamination steel” (CRML) are usually intended for applications in which the stamped laminations or assembled core structures for electrical equipment are annealed to develop the desired core loss and permeability characteristics.
1.2 This steel is produced to maximum specific core-loss values and is intended primarily for commercial power frequency (50- and 60-Hz) applications in magnetic devices. Specific core-loss and permeability characteristics in conformance with this specification are developed through heat treatment by the user.
1.3 Non-guaranteed core-loss types, usually made to controlled chemical compositions, are available but are not covered by this specification.
1.4 Higher quality core-loss types are low carbon, silicon-iron, or silicon-aluminum-iron alloys containing up to about 2.5 % silicon and less than 1 % aluminum. These steels are usually given a critical reduction on a temper-mill to yield specified magnetic properties after a suitable lamination anneal. These products, typically called semiprocessed magnetic lamination steel, are classified by the ASTM Code Letter D in accordance with Practice A664.
1.5 The values stated in SI units are to be regarded as standard. The values given in parentheses are mathematical conversions to customary (cgs-emu and inch-pound) units which are provided for information only and are not considered standard.
1.6 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.
1.7 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
тел.: (495) 223-46-76 (прямой московский номер)