ASTM A831/A831M-95(2000)
Standard Specification for Austenitic and Martensitic Stainless Steel Bars, Billets, and Forgings for Liquid Metal Cooled Reactor Core Components (Withdrawn 2005)
5 стр.
Отменен
Печатное изданиеЭлектронный (pdf)
93.60 $ (включая НДС 20%)
Разработчик:
Зарубежные/ASTM
ICS:
77.140.20 Stainless. Including alloyed steels, corrosion-resistant steels, heat-resisting steels, etc. / Высококачественные стали
Сборник (ASTM):
01.03 Steel--Plate, Sheet, Strip, Wire; Stainless Steel Bar / Сталь - Плиты, листы, штрипсы, проволока; сортовой прокат из нержавеющей стали
Тематика:
Steel--Structural, Tubes, Plate, Coated
Описание
Причина отмены

This specification covers hot- and cold-finished austenitic and martensitic stainless steel bars, billets, and forgings intended for use in manufacturing core components used at high temperatures in liquid metal cooled nuclear reactors.

Formerly under the jurisdiction of A01 on Steel, Stainless Steel and Related Alloys, this specification was withdrawn in March 2005. This specification is being withdrawn without replacement due to its limited use in the industry.

Область применения

1.1 This specification covers hot- and cold-finished austenitic and martensitic stainless steel bars, billets, and forgings intended for use in manufacturing core components used at high temperatures in liquid metal cooled nuclear reactors.

1.2 The bars, billets, and forgings are intended for machining, welding, hot- and cold-forming operations.

1.3 The values stated in either inch-pound units or SI units are to be regarded separately as standard. Within the text, the SI units are shown in brackets. The values stated in each system are not exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the specification.

1.4 This specification and the applicable material specifications are expressed in both inch-pound and SI units. However, unless the order specifies the applicable "M" specification designation (SI units), the material shall be furnished in inch-pound units.

Ключевые слова:
austenitic stainless steel; high temperature core components; martensitic stainless steel; nuclear applications; stainless steel bars; stainless steel billets; stainless steel forgings