ASTM A840/A840M-00(2006)
Standard Specification for Fully Processed Magnetic Lamination Steel (Withdrawn 2011)
4 стр.
Отменен
Печатное изданиеЭлектронный (pdf)
84.24 $ (включая НДС 20%)
Разработчик:
Зарубежные/ASTM
ICS:
77.140.50 Flat. Including plate, sheet and strip / Стальной листовой прокат и полуфабрикаты. Включая плиты, листы и полосы
Сборник (ASTM):
03.07 Magnetic Properties / Магнитные свойства
Тематика:
Electrical and Magnetic Conductors, Electrical Contacts
Описание
Причина отмены

This specification covers cold-rolled carbon steel coils or strip used in the fully processed condition in magnetic lamination applications.

Formerly under the jurisdiction of Committee A06 on Magnetic Properties, this specification was withdrawn in May 2011. This standard is being withdrawn with no replacement because of a lack of commercial/technical interest.

Реферат

This specification covers standard requirements for flat-rolled carbon steel used in the fully processed condition in magnetic lamination applications. Steels supplied to this specification normally do not require further heat treatment by the user. There are no chemical requirements for these lamination steels. Instead the steels shall be produced to specified maximum core-loss values. Steels produced to this specification are available in thicknesses of 0.0185 in. (0.47 mm) and 0.025 in. (0.64 mm). For each thickness there are two core-loss types. The core loss is determined using the Epstein test method at a frequency of 60 Hz and a maximum flux density of 15 kG. In addition to the magnetic property requirements, dimensional tolerances, lamination factors and mechanical hardnesses are specified.

Область применения

1.1 This specification covers cold-rolled carbon steel coils or strip used in the fully processed condition in magnetic lamination applications.

1.2 This steel is produced to specified maximum core-loss values and is intended primarily for commercial power frequency (50- and 60-Hz) applications in magnetic devices. Desirable core-loss and permeability characteristics are developed during mill processing, so further heat treatment by the purchaser is not necessary for most uses.

1.3 Fully processed magnetic lamination steels are flat-rolled low carbon iron alloys having 1 % maximum silicon and 0.4 % maximum aluminum.

1.4 The values stated in customary (cgs-emu and inch-pound) units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units which are provided for information only and are not considered standard.

Ключевые слова:
carbon steel sheet; cold-rolled lamination steel; cold-rolled magnetic lamination steel; fully processed; lamination steel; magnetic lamination steel