ASTM A926-03(2014)
Standard Test Method for Comparing the Abrasion Resistance of Coating Materials for Corrugated Metal Pipe (Withdrawn 2016)
5 стр.
Отменен
Электронный (pdf)Печатное издание
96.72 $ (включая НДС 20%)
Разработчик:
Зарубежные/ASTM
ICS:
19.060 Mechanical. Including testing equipment / Механические испытания. Включая испытательное оборудование25.220.01 Surface treatment and coating in general / Обработка и покрытие поверхности в целом
Сборник (ASTM):
01.06 Coated Steel Products / Изделия из облицовочной стали
Тематика:
Steel--Structural, Tubes, Plate, Coated
Описание
Причина отменыFormerly under the jurisdiction of Committee A05 on Metallic-Coated Iron and Steel Products, this test method was withdrawn in May 2016. This standard is being withdrawn without replacement due to its limited use by industry.

This test method covered a procedure for comparing materials used for coating, paving and lining corrugated metal pipe by use of a bed load abrasion testing machine. The procedure attempts to simulate the effect of stone, gravel and sand carried by a stream through corrugated metal pipe.

Значение и использование

4.1 This test method provides a means of determining an abrasion rate (weight and calculated average thickness loss) when comparing materials, coatings, pavings, or linings under test conditions that will be subjected to abrasive bed loads. The importance of this information is recognized when dealing with culverts, storm and sanitary sewer applications, although the last two generally do not have the same degree of abrasion due to the flatter slopes and less bed loads than culverts. Specifically, the invert of these types of pipe, regardless of the material used, can be exposed to flows containing abrasive bed loads or solid particulates that cause wearing of the pipe wall.

4.2 By subjecting materials to wear in the bed load abrasion machine with a controlled bed load charge made up of fine aggregate and coarse aggregate over a specified period, a comparison of the resistance between materials can be established.

4.3 This test method does not simulate the effect of abrasive material striking the upstream face of corrugations, as would be typical for coating materials which do not completely fill the corrugations.

Note 1: Caution: This test method uses specific quantitative values to encourage repetitive results and does not consider varying bed load characteristics, ratio of water to bed load, velocity, time or actual field conditions, and the effect of exposed edges on laminates. The user must use extreme care in comparing one test result to another because of these and other variables.

Область применения

1.1 This test method covers a procedure for comparing materials used for coating, paving and lining corrugated metal pipe by use of a bed load abrasion testing machine. The procedure attempts to simulate the effect of stone, gravel and sand carried by a stream through corrugated metal pipe.

1.2 The values stated in inch-pound units are to be regarded as standard. The SI units given in parentheses are for information only.

1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

Ключевые слова:
abrasion resistance of pipe coatings; coatings—;abrasion; corrugated metal pipe; resistance of coating materials to abrasion; steel pipe coatings