ASTM B737-10(2015)
Standard Specification for Hot-Rolled and/or Cold-Finished Hafnium Rod and Wire
4 стр.
Заменен
Печатное изданиеЭлектронный (pdf)
84.24 $ (включая НДС 20%)
Разработчик:
Зарубежные/ASTM
ICS:
77.150.99 Other products of non-ferrous metals / Продукция из цветных металлов прочая
Сборник (ASTM):
02.04 Nonferrous Metals – Nickel, Titanium, Lead, Tin, Zinc, Zirconium, Precious, Reactive, Refractory Metals and Alloys: Materials for Thermostats, Electrical Heating and Resistance Contact, and Connectors / Цветные металлы - Никель, Кобальт, Свинец, Олово, Цинк, Кадмий, Драгоценные металлы, химически активные металлы, Тугоплавкие металлы и сплавы, Материалы для Термостатов, Электронагревательных приборов, Контактов, Соединительные устройств
Тематика:
Other Nonferrous Metals
Описание
Значение и использование

15.1 For the purpose of determining compliance with the specified limits for requirements of the properties listed in the following table, an observed value or a calculated value shall be rounded as indicated in accordance with the rounding methods of Practice E29.

Property

Rounded Unit for Observed
or Calculated Value

 Chemical composition, and tolerances (when expressed as decimals)

nearest unit in the last right-hand place of figures of the specified limit

 Tensile strength and yield strength

nearest 1000 psi (10 MPa)

 Elongation

nearest 1 %

Реферат

This specification covers hot-, cold-, or both hot- and cold-rolled hafnium rods and wires in either one of two grades. All grades should be in the recrystallization annealed condition unless specified otherwise. The materials should be made from ingots produced by vacuum melting in an electron beam or consumable arc furnaces, or both, of a type conventionally used for reactive metals. Samples for chemical composition tests should be taken from the top, middle, and bottom of the ingots. The requirements for mechanical properties do not apply to wires. Corrosion tests shall be done in water. All rods should be furnished in mechanically descaled and pickled, centerless ground and pickled, or centerless ground, pickled, and oxidized surface finish, while wires should be furnished in either conditioned and pickled or conditioned, pickled, and oxidized surface finish.

Область применения

1.1 This specification covers hot- or cold-worked hafnium rod and wire.

1.2 This specification contains two material grades, one specifically for nuclear applications (Grade R1) and one for commercial alloying applications (Grade R3).

1.3 The products covered include the following:

1.3.1 Rod 3/8 to 1 in. (9.5 to 25 mm) in diameter.

1.3.2 Wire less than 3/8 in. (9.5 mm) in diameter.

1.4 Unless a single unit is used, for example, corrosion mass gain in mg/dm2, the values stated in either inch-pound or SI units are to be regarded separately as standard. The values stated in each system are not exact equivalents; therefore, each system must be used independently of the other. SI values cannot be mixed with inch-pound values.

1.5 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

Ключевые слова:
hafnium; hafnium alloy; rod; wire;