ASTM C1239-00(2005)
Standard Practice for Reporting Uniaxial Strength Data and Estimating Weibull Distribution Parameters for Advanced Ceramics
19 стр.
Заменен
Печатное изданиеЭлектронный (pdf)
107.64 $ (включая НДС 20%)
Разработчик:
Зарубежные/ASTM
ICS:
81.060.99 Other standards related to ceramics / Керамика, прочие аспекты
Сборник (ASTM):
15.01 Refractories, Activated Carbon; Advanced Ceramics / Огнеупорные материалы; Активированный уголь, Высококачественная керамика
Тематика:
Glass, Ceramics
Описание
Область применения

1.1 This practice covers the evaluation and subsequent reporting of uniaxial strength data and the estimation of probability distribution parameters for advanced ceramics that fail in a brittle fashion. The failure strength of advanced ceramics is treated as a continuous random variable. Typically, a number of test specimens with well-defined geometry are failed under well-defined isothermal loading conditions. The load at which each specimen fails is recorded. The resulting failure stresses are used to obtain parameter estimates associated with the underlying population distribution. This practice is restricted to the assumption that the distribution underlying the failure strengths is the two-parameter Weibull distribution with size scaling. Furthermore, this practice is restricted to test specimens (tensile, flexural, pressurized ring, etc.) that are primarily subjected to uniaxial stress states. Section 8 outlines methods to correct for bias errors in the estimated Weibull parameters and to calculate confidence bounds on those estimates from data sets where all failures originate from a single flaw population (that is, a single failure mode). In samples where failures originate from multiple independent flaw populations (for example, competing failure modes), the methods outlined in Section 8 for bias correction and confidence bounds are not applicable.

1.2 Measurements of the strength at failure are taken for one of two reasons: either for a comparison of the relative quality of two materials, or the prediction of the probability of failure (or, alternatively, the fracture strength) for a structure of interest. This practice will permit estimates of the distribution parameters that are needed for either. In addition, this practice encourages the integration of mechanical property data and fractographic analysis.

1.3 This practice includes the following:

Section
Scope 1
Referenced Documents 2
Terminology 3
Summary of Practice 4
Significance and Use 5
Outlying Observations 6
Maximum Likelihood Parameter Estimators for Competing Flaw Distributions7
Unbiasing Factors and Confidence Bounds 8
Fractography 9
Examples 10
Keywords 11
Computer Algorithm MAXL X1
Test Specimens with Unidentified Fracture Origins X2

1.4 The values stated in SI units are to be regarded as the standard.

Ключевые слова:
advanced ceramics; censored data; confidence bounds; fractography; fracture origin; maximum likelihood; strength; unbiasing factors; Weibull characteristic strength; Weibull modulus; Weibull scale parameter; Weibull statistics