ASTM C1272-11a
Standard Specification for Heavy Vehicular Paving Brick
4 стр.
Заменен
Электронный (pdf)Печатное издание
84.24 $ (включая НДС 20%)
Разработчик:
Зарубежные/ASTM
ICS:
93.080.20 Road. Including asphalts, road pavements, etc. / Дорожно-строительные материалы. Включая асфальт, дорожные покрытия и т.д.
Сборник (ASTM):
04.05 Chemical–Resistant Nonmetallic Materials; Vitrified Clay Pipe; Concrete Pipe; Fiber-Reinforced Cement Products; Mortars and Grouts; Masonry; Precast Concrete / Химически устойчивые неметаллические материалы; Глазированные керамические трубы; Трубы бетонные; изделия из фиброцемента; Известковые цементные растворы; Монолитный бетон; Сборный бетон
Тематика:
Masonry
Описание
Реферат

This specification covers heavy vehicular paving bricks designed for use in streets, commercial driveways, aircraft taxiways, and other places where there is a high volume of heavy vehicular traffic. The bricks should be manufactured from clay, shale, or similar naturally occurring earthy substances and subjected to firing. The high temperature heat treatment should develop sufficient fired bonds between the material particles to produce the required strength and durability. The bricks may also be shaped by extruding, molding, or pressing during manufacture and may have spacing lugs, chamfered edges, or both. The materials are classified into two types according to the intended installation and should all conform to the required values of freeze thaw resistance, abrasion resistance, skid resistance, coring, chips or cracks, and efflorescence.

Область применения

1.1 This specification covers brick intended for use as a paving material in areas with a high volume of heavy vehicular traffic. The units are designed for use in such places as streets, commercial driveways, and aircraft taxiways. These units are not intended for applications covered by Specifications C410 or C902.

1.2 Units are manufactured from clay, shale, or similar naturally occurring earthy substances and subjected to a heat treatment at elevated temperatures (firing). The heat treatment must develop sufficient fired bond between the particulate constituents to provide the strength and durability requirements of this specification (see Terminology C1232).

1.3 Brick may be shaped during manufacture by extruding, molding, or pressing. Brick may have spacing lugs, chamfered edges, or both.

1.4 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.

Ключевые слова:
brick; fired masonry units; pavement surfaces: Heavy vehicular paving brick; Masonry units--specifications; Brick--specifications; Pavement surfaces--specifications; Vehicular paving brick