ASTM C133-97(2008)e1
Standard Test Methods for Cold Crushing Strength and Modulus of Rupture of Refractories
Стандартные методы испытания для определения прочности при дроблении в холодном состоянии и предела прочности при изгибе огнеупоров
6 стр.
Заменен
Печатное изданиеЭлектронный (pdf)
93.60 $ (включая НДС 20%)
Разработчик:
Зарубежные/ASTM
ICS:
81.080 Refractories. Including ceramic refractories / Огнеупоры. Включая огнеупоры из керамики
Сборник (ASTM):
15.01 Refractories, Activated Carbon; Advanced Ceramics / Огнеупорные материалы; Активированный уголь, Высококачественная керамика
Тематика:
Refractories
Описание
Значение и использование

The cold strength of a refractory material is an indication of its suitability for use in refractory construction. (It is not a measure of performance at elevated temperatures.)

These test methods are for determining the room temperature flexural strength in 3-point bending (cold modulus of rupture) or compressive strength (cold crushing strength), or both, for all refractory products.

Considerable care must be used to compare the results of different determinations of the cold crushing strength or modulus of rupture. The specimen size and shape, the nature of the specimen faces (that is, as-formed, sawed, or ground), the orientation of those faces during testing, the loading geometry, and the rate of load application, may all significantly affect the numerical results obtained. Comparisons of the results between different determinations should not be made if one or more of these parameters differ between the two determinations.

The relative ratio of the largest grain size to the smallest specimen dimension may significantly affect the numerical results. For example, smaller, cut specimens containing large grains may present different results than the bricks from which they were cut. Under no circumstances should 6- by 1- by 1-in. (152- by 25- by 25-mm) specimens be prepared and tested for materials containing grains with a maximum grain dimension exceeding 0.25 in. (6.4 mm).

This test method is useful for research and development, engineering application and design, manufacturing process control, and for developing purchasing specifications.

Область применения

1.1 These test methods cover the determination of the cold crushing strength and the modulus of rupture (MOR) of dried or fired refractory shapes of all types.

1.2 The test methods appear in the following sections:

Test Method Sections
Cold Crushing Strength 4 to 9
Modulus of Rupture 10 to 15

1.3 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.

1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

Ключевые слова:
crushing strength; modulus of rupture; monolithic refractories; refractory brick; room temperature; Compression testing--refractory products; Crushing strength; Modulus of rupture (MOR)--refractories; Refractories (brick and shapes)--modulus of rupture; Refractories (bricks and shapes)