ASTM C1581-04
Standard Test Method for Determining Age at Cracking and Induced Tensile Stress Characteristics of Mortar and Concrete under Restrained Shrinkage
6 стр.
Заменен
Печатное изданиеЭлектронный (pdf)
93.60 $ (включая НДС 20%)
Разработчик:
Зарубежные/ASTM
ICS:
91.100.30 Concrete. Including admixtures / Бетон и изделия из бетона
Сборник (ASTM):
04.02 Concrete and Aggregates / Бетон и заполнители для бетона
Тематика:
Cement & Concrete
Описание
Значение и использование

This test method is for relative comparison of materials and is not intended to determine the age at cracking of mortar or concrete in any specific type of structure, configuration, or exposure.

This test method is applicable to mixtures with aggregates of 0.5-in. (13-mm) maximum nominal size or less.

This test method is useful for determining the relative likelihood of early-age cracking of different cementitious mixtures and for aiding in the selection of cement-based materials that are less likely to crack under retrained shrinkage. Actual cracking tendency in service depends on many variables including type of structure, degree of restraint, rate of property development, construction and curing methods, and environmental conditions.

This test method can be used to determine the relative effects of material variations on induced tensile stresses and cracking potential. These variations can include, but are not limited to, aggregate source, aggregate gradation, cement type, cement content, water content, supplementary cementing materials, or chemical admixtures.

For materials that have not cracked during the test, the rate of tensile stress development at the time the test is terminated provides a basis for comparison of the materials.

Область применения

1.1 This test method covers the laboratory determination of the age at cracking and induced tensile stress characteristics of mortar or concrete specimens under restrained shrinkage. The procedure can be used to determine the effects of variations in the proportions and material properties of mortar or concrete on cracking due to both drying shrinkage and deformations caused by autogenous shrinkage and heat of hydration.

1.2 This test method is not intended for expansive materials.

1.3 The values stated in inch-pound units are to be regarded as standard. The values shown in parenthesis are in SI units and are given for information only.

1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and to determine the applicability of regulatory limitations prior to use. (Warning-Fresh hydraulic cementitious mixtures are caustic and may cause chemical burns to skin and tissue upon prolonged exposure.)

Ключевые слова:
Cracking; restrained shrinkage; ring test; shrinkage; tensile stress