This test method may be used for routine inspection purposes by subjecting a required number of specimens to the test conditions for a specified time and noting the number that fail. The cracking obtained with the test reagent is indicative of what may be expected from a wide variety of surface-active agents, soaps, and organic substances that are not absorbed appreciably by the polymer.
Environmental stress-cracking is a property that is highly dependent upon the nature and level of the stresses applied and on the thermal history of the specimen (1). Under the conditions of the test method, high local multiaxial stresses are developed through the introduction of a controlled imperfection (2,3). Environmental stress-cracking has been found to occur most readily under such conditions.
Note 2—Different types of polyethylene plastics as defined in Specification D 1248
Information from this test method is not intended to be used for direct application to engineering problems.
Note 3—Caution should be used in comparing and ranking various ethylene plastics into distinct and separate groups by this test method (see Section 13 and Note 12).
As thermal history is recognized as an important variable, test results by this test method employing laboratory molded samples cannot necessarily be expected to show agreement with test results from samples obtained by other means. The true performance potential of a given ethylene plastic may, however, best be determined with specimens obtained from commercially prepared items (5).
Condition | Specimen Thickness | Notch Depth | Bath Temperature, °C | |||
---|---|---|---|---|---|---|
mmA | in. | mmA | in. | |||
AB | min | 3.00 | 0.120 | 0.50 | 0.020 | 50 |
max | 3.30 | 0.130 | 0.65 | 0.025 | ||
BB | min | 1.84 | 0.0725 | 0.30 | 0.012 | 50 |
max | 1.97 | 0.0775 | 0.40 | 0.015 | ||
CC | min | 1.84 | 0.0725 | 0.30 | 0.012 | 100C |
max | 1.97 | 0.0775 | 0.40 | 0.015 |
A Dimensional values are not exactly equivalent. However, for referee purposes the metric units shall apply.
B For referee purposes, concentration of Igepal will be consistent with the appropriate material standard. If no concentration is given, then 10 % volume solution shall be used.
C At a temperature of 100°C, a full-strength reagent, rather than an aqueous solution of a reagent, is generally used because solutions tend to change their compositions by water evaporation losses during the period of test.
Область применения1.1 This test method covers the determination of the susceptibility of ethylene plastics, as defined in Terminology D 883
1.2 The values stated in SI units are to be regarded as standard.
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use. Note 1—There is no similar or equivalent ISO standard.