ASTM D2457-08e1
Standard Test Method for Specular Gloss of Plastic Films and Solid Plastics
6 стр.
Заменен
Печатное изданиеЭлектронный (pdf)
96.72 $ (включая НДС 20%)
Разработчик:
Зарубежные/ASTM
ICS:
83.140.10 Films. Including plates / Пленки и листы. Включая пластины
Сборник (ASTM):
08.01 Plastics (I): C1147–D3159 / Пластмасса (I): C1147–D3159
Тематика:
Plastics
Описание
Значение и использование

Specular gloss is used primarily as a measure of the shiny appearance of films and surfaces. Precise comparisons of gloss values are meaningful only when they refer to the same measurement procedure and same general type of material. In particular, gloss values for transparent films should not be compared with those for opaque films, and vice versa. Gloss is a complex attribute of a surface which cannot be completely measured by any single number.

Specular gloss usually varies with surface smoothness and flatness. It is sometimes used for comparative measurements of these surface properties.

Область применения

1.1 This test method describes procedures for the measurement of gloss of plastic films and solid plastics, both opaque and transparent. It contains four separate gloss angles (Note 1):

1.1.1 60-deg, recommended for intermediate-gloss films,

1.1.2 20-deg, recommended for high-gloss films,

1.1.3 45-deg, recommended for intermediate and low-gloss films, and

1.1.4 75-deg, recommended for plastic siding and soffit.

Note 1—The 75-deg, 60-deg, and 20-deg apparatus and method of measurement duplicate those in Test Method D523; those for the 45° procedure are similarly taken from Test Method C346.

1.2 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

Note 2—There is no similar or equivalent ISO standard.

Ключевые слова:
gloss; plastic films; solid plastics; Solid plastics; Gloss; Plastic sheet and film