ASTM D3769-05
Standard Test Method for Microcellular Urethanes--High Temperature Sag
3 стр.
Заменен
Печатное изданиеЭлектронный (pdf)
84.24 $ (включая НДС 20%)
Разработчик:
Зарубежные/ASTM
ICS:
83.100 Cellular materials / Поропласты
Сборник (ASTM):
08.02 Plastics (II): D3222–D5083 / Пластмасса (II): D3222–D5083
Тематика:
Plastics
Описание
Значение и использование

This test method is used to indicate the deformation tendency of microcellular materials that may occur during paint application in an assembly plant operation. Since a standard specimen is used, heat sag measurements cannot be assumed to be exactly those which will occur on a part during or after the paint application and baking operation of an assembly process.

Before proceeding with this test method, reference should be made to the specification of the material being tested. Any test specimen preparation, conditioning, or dimensions, or combination thereof, and testing parameters covered in the materials specification shall take precedence over those mentioned in these test methods. If there are no material specifications, then the default conditions apply.

Note 2—This test method is applicable to solid urethanes.

Область применения

1.1 This test method covers the procedure and apparatus for measuring high-temperature sag of microcellular urethane materials.

1.2 The values stated in SI units are to be regarded as standard.

This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

Note 1

There is no similar or equivalent ISO standard to this test method.

Ключевые слова:
deformation; high-temperature; microcellular; sag; urethane