ASTM D5048-14
Standard Test Method for Measuring the Comparative Burning Characteristics and Resistance to Burn-Through of Solid Plastics Using a 125-mm Flame
7 стр.
Заменен
Печатное изданиеЭлектронный (pdf)
96.72 $ (включая НДС 20%)
Разработчик:
Зарубежные/ASTM
ICS:
83.080.01 Plastics in general / Пластмассы в целом13.220.40 Ignitability and burning behaviour of materials and products / Воспламеняемость, поведение материалов и продуктов при горении
Сборник (ASTM):
08.02 Plastics (II): D3222–D5083 / Пластмасса (II): D3222–D5083
Тематика:
Plastics
Описание
Значение и использование

5.1 The test results represent afterflame plus afterglow time, in seconds, for a material under the conditions of the test. The test results for plaques also indicate whether or not the specified flame will burn through a material.

5.2 The effect of material thickness, colors, additives, deterioration, and possible loss of volatile components is measurable.

5.3 The burning characteristics vary with thickness. Compare test data with data for materials of similar thickness only.

5.4 The results serve as a reference for comparing the relative performance of materials and can be an aid in material selection.

5.5 In this test method, the specimens are subjected to specific laboratory test conditions. If different test conditions are substituted or the end-use conditions are changed, it will not always be possible by or from this test method to predict changes in the fire-test-response characteristics measured. Therefore, the results are valid only for the fire-test-exposure conditions described in this test method.

Область применения

1.1 This fire-test-response test method covers a small-scale laboratory procedure for determining the relative burning characteristics and the resistance to burn-through of plastics using small bar and plaque specimens exposed to a 125-mm (500-W nominal) flame.

Note 1This test method is equivalent to IEC 60695-11-20.
Note 2For additional information on comparative burning characteristics of solid plastics in a vertical position, see Test Method D3801.

1.2 This test method was developed for polymeric materials used for parts in devices and appliances. The results are intended to serve as a preliminary indication of their acceptability with respect to flammability for a particular application. The final acceptance of the material is dependent upon its use in complete equipment that conforms with the standards applicable to such equipment.

1.3 The classification system described in Appendix X1 is intended for quality assurance and the preselection of component materials for products.

1.4 If found to be appropriate, it is suitable to apply the requirements to other nonmetallic materials. Such application is outside the scope of this technical committee.

1.5 This test method is not intended to cover plastics when used as materials for building construction or finishing.

1.6 Fire testing is inherently hazardous. Adequate safeguards for personnel and property shall be employed in conducting these tests.

1.7 This standard is used to measure and describe the response of materials, products, or assemblies to heat and flame under controlled conditions, but does not by itself incorporate all factors required for fire hazards or fire risk assessment of materials, products, or assemblies under actual fire conditions.

1.8 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use. See 6.1.1 for a specific hazard statement.

Ключевые слова:
burning characteristics; flammability; plastics; solid; resistance to burn-through; small-scale burning tests; vertical burning tests