ASTM E2283-07
Standard Practice for Extreme Value Analysis of Nonmetallic Inclusions in Steel and Other Microstructural Features
8 стр.
Заменен
Печатное изданиеЭлектронный (pdf)
96.72 $ (включая НДС 20%)
Разработчик:
Зарубежные/ASTM
ICS:
77.040.99 Other methods of testing of metals / Методы испытания металлов прочие
Сборник (ASTM):
03.01 Metals -- Mechanical Testing; Elevated and Low-Temperature Tests; Metallography / Металлы - Механические испытания, Испытания при высоких и низких температурах, Металлография
Тематика:
Physical & Mechanical Testing
Описание
Значение и использование

This practice is used to assess the indigenous inclusions or second-phase constituents in metals using extreme value statistics.

It is well known that failures of mechanical components, such as gears and bearings, are often caused by the presence of large nonmetallic oxide inclusions. Failure of a component can often be traced to the presence of a large inclusion. Predictions related to component fatigue life are not possible with the evaluations provided by standards such as Test Methods E 45, Practice E 1122, or Practice E 1245. The use of extreme value statistics has been related to component life and inclusion size distributions by several different investigators (3-8). The purpose of this practice is to create a standardized method of performing this analysis.

This practice is not suitable for assessing the exogenous inclusions in steels and other metals because of the unpredictable nature of the distribution of exogenous inclusions. Other methods involving complete inspection such as ultrasonics must be used to locate their presence.

Область применения

1.1 This practice describes a methodology to statistically characterize the distribution of the largest indigenous nonmetallic inclusions in steel specimens based upon quantitative metallographic measurements. The practice is not suitable for assessing exogenous inclusions.

1.2 Based upon the statistical analysis, the nonmetallic content of different lots of steels can be compared.

1.3 This practice deals only with the recommended test methods and nothing in it should be construed as defining or establishing limits of acceptability.

1.4 The measured values are stated in SI units. For measurements obtained from light microscopy, linear feature parameters shall be reported as micrometers, and feature areas shall be reported as micrometers.

1.5 The methodology can be extended to other materials and to other microstructural features.

1.6 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

Ключевые слова:
extreme value statistics; inclusion length; maximum inclusion length; maximum likelihood method; Extreme value statistics; Inclusion length; Inclusions; Indigenous inclusions; Maximum inclusion length; Metallographic analysis/inspection; Microstructures; Nonmetallic inclusions; Statistical methods--metals/alloys; Steel; Value analysis (VA)