ASTM E618-07(2018)
Standard Test Method for Evaluating Machining Performance of Ferrous Metals Using an Automatic Screw/Bar Machine (Withdrawn 2023)
11 стр.
Отменен
Электронный (pdf)Печатное издание
129.48 $ (включая НДС 20%)
Разработчик:
Зарубежные/ASTM
ICS:
25.080.10 Lathes / Токарные станки
Сборник (ASTM):
01.05 Steel--Bars, Forgings, Bearing, Chain, Tool / Сталь - Прутья, Поковки и Заготовки, Балки
Тематика:
Steel--Structural, Tubes, Plate, Coated
Описание
Причина отменыThis test method covered a production-type test for evaluating the machining performance of ferrous metals as they were used in single-spindle or multiple-spindle automatic screw machines. It was based on producing parts of a standard design in such machines to uniform levels of quality with respect to surface roughness and size variation.

Formerly under the jurisdiction of Committee A01 on Steel, Stainless Steel and Related Alloys, this test method was withdrawn in November 2023. This standard is being withdrawn without replacement due to its limited use by industry.

Значение и использование

5.1 This test method can be used to evaluate the machining performance of a single grade or type of metal or to compare one grade or type with another.

5.1.1 The machining performance of the test metal is measured by the maximum rate at which test pieces can be produced within specified surface roughness and dimensional limits for a specified length of time and also by the cutting speed and tool feed employed to attain that rate.

5.1.2 The relative machining performance of the various metals tested using this test method may be evaluated only at operating conditions that produce test pieces of like quality with respect to surface roughness and dimensional limits for comparable periods of machining time.

Область применения

1.1 This test method covers a production-type test for evaluating the machining performance of ferrous metals as they are used in single-spindle or multiple-spindle automatic screw machines. It is based on producing parts of a standard design in such machines to uniform levels of quality with respect to surface roughness and size variation. The standard test piece, designed for this test, is machined from bars using a specified number of tools in a specified sequence. Nothing in this test method should be construed as defining or establishing limits of acceptability for any grade or type of metal.

1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.

1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.

1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.