ASTM G168-00
Standard Practice for Making and Using Precracked Double Beam Stress Corrosion Specimens
10 стр.
Заменен
Печатное изданиеЭлектронный (pdf)
93.60 $ (включая НДС 20%)
Разработчик:
Зарубежные/ASTM
ICS:
77.060 Corrosion of metals / Коррозия металлов
Сборник (ASTM):
03.02 Corrosion of Metals; Wear and Erosion / Коррозия металлов; Износ и разрушение (эрозия) металлов
Тематика:
Corrosion & Wear
Описание
Область применения

1.1 This practice covers procedures for fabricating, preparing, and using precracked double beam stress corrosion test specimens. This specimen configuration was formerly designated the double cantilever beam (DCB) specimen. Guidelines are given for methods of exposure and inspection.

1.2 The precracked double beam specimen, as described in this practice, is applicable for evaluation of a wide variety of metals exposed to corrosive environments. It is particularly suited to evaluation of products having a highly directional grain structure, such as rolled plate, forgings, and extrusions, when stressed in the short transverse direction.

1.3 The precracked double beam specimen may be stressed in constant displacement by bolt or wedge loading or in constant load by use of proof rings or dead weight loading. The precracked double beam specimen is amenable to exposure to aqueous or other liquid solutions by specimen immersion or by periodic dropwise addition of solution to the crack tip, or exposure to the atmosphere.

1.4 This practice is concerned only with precracked double beam specimen and not with the detailed environmental aspects of stress corrosion testing, which are covered in Practices G35, G36, G37, G41, G44, and G50.

1.5 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

Ключевые слова:
rack growth rate; double cantilever beam specimen; KISCC; plateau velocity; precracked double beam specimen; precracked specimens; stress corrosion cracking; threshold stress intensity