ASTM A564/A564M-10
Standard Specification for Hot-Rolled and Cold-Finished Age-Hardening Stainless Steel Bars and Shapes
Стандартные технические условия на горячекатаные и упрочненные старением с холодной отделкой прутки и профили из нержавеющей стали
7 стр.
Заменен
Печатное изданиеЭлектронный (pdf)
96.72 $ (включая НДС 20%)
Разработчик:
Зарубежные/ASTM
ICS:
77.140.70 Steel. Including sections / Стальные профили. Включая секции77.140.60 Steel bars and rods / Стальные прутки и катанка
Сборник (ASTM):
01.03 Steel--Plate, Sheet, Strip, Wire; Stainless Steel Bar / Сталь - Плиты, листы, штрипсы, проволока; сортовой прокат из нержавеющей стали
Тематика:
Steel--Structural, Tubes, Plate, Coated
Описание
Реферат

This specification covers bars and shapes of age-hardening stainless steels. Hot-finished or cold-finished rounds, squares, hexagons, bar shapes, angles, tees, and channels are included. These shapes may be produced by hot rolling, extruding, or forging. Type 631 and 632 stainless steels contain a large amount of ferrite in the microstructure and can have low ductility in forgings and large diameter bars. Material of types other than XM-16, XM-25, and Type 630 shall be furnished in the solution-annealed condition, or in the equalized and oven-tempered condition. Types 630, XM-16, and XM-25 may be furnished in the solution-annealed or age-hardened condition. Type UNS S46910 shall be furnished in solution annealed, cold-worked or aged-hardened condition. Shapes may be subjected to either Class A or Class C preparation for removal of visible surface imperfections. The material shall be subjected to tension, impact, and hardness tests.

Область применения

1.1 This specification covers bars and shapes of age-hardening stainless steels. Hot-finished or cold-finished rounds, squares, hexagons, bar shapes, angles, tees, and channels are included; these shapes may be produced by hot rolling, extruding, or forging. Billets or bars for reforging may be purchased to this specification.

1.2 These steels are generally used for parts requiring corrosion resistance and high strength at room temperature, or at temperatures up to 600°F [315°C]; 700°F [370°C] for Type 632; 840°F [450°C] for Type UNS S46910. They are suitable for machining in the solution-annealed condition after which they may be age-hardened to the mechanical properties specified in Section 7 without danger of cracking or distortion. Type XM-25 is machinable in the as-received fully heat treated condition. Type UNS S46910 is suitable for machining in the solution-annealed, cold-worked, and aged-hardened condition.

1.3 Types 631 and 632 contain a large amount of ferrite in the microstructure and can have low ductility in forgings and larger diameter bars. Applications should be limited to small diameter bar.

1.4 The values stated in either inch-pound units or SI (metric) units are to be regarded separately as standards; within the text and tables, the SI units are shown in [brackets]. The values stated in each system are not exact equivalents; therefore, each system must be used independent of the other. Combining values from the two systems may result in nonconformance with the specification.

Ключевые слова:
age-hardening stainless steel; precipitation hardening stainless steel; stainless steel bars; stainless steel shapes; Age-hardening alloys--specifications; Cold-finished steel bars--specifications; Corrosive service applications--bars/rods/shapes; High-temperature service applications--steel bars; Hot-rolled stainless steel bars--specifications; Precipitation-hardening metals/alloys--specifications; Stainless steel bars/billets--specifications; Steel bars and shapes--specifications; Steel bars/shapes/wires; Udimet alloy