ASTM D6676-01e1
Standard Test Method for Cathodic Disbonding of Exterior Pipeline Coatings at Elevated Temperatures Using Interior Heating (Withdrawn 2010)
8 стр.
Заменен
Электронный (pdf)Печатное издание
96.72 $ (включая НДС 20%)
Разработчик:
Зарубежные/ASTM
ICS:
19.040 Environmental. Including testing equipment / Климатические испытания. Включая испытательное оборудование25.220.01 Surface treatment and coating in general / Обработка и покрытие поверхности в целом
Сборник (ASTM):
06.02 Paint –– Products and Applications; Protective Coatings; Pipeline Coatings / Красители – Продукты и их применение; Защитные покрытия; Покрытия для трубопровода
Тематика:
Paints & Related Coatings
Описание
Причина отмены

This test method describes an accelerated procedure for determining comparative characteristics of coating systems applied to the exterior of steel pipe for the purpose of preventing or mitigating corrosion that may occur in underground or immersion where the pipe is carrying heated media and is under cathodic protection. This test method is intended for use with samples of coated pipe, or with a specimen cut from the section of coated pipe or flat plates, and is applicable to such samples when the coating is characterized by function as an electrical barrier.

Formerly under the jurisdiction of Committee D01 on Paint and Related Coatings, Materials, and Applicaitons, this test method was withdrawn in January 2010 in accordance with section 10.5.3.1 of the Regulations Governing ASTM Technical Committees, which requires that standards shall be updated by the end of the eighth year since the last approval date.

Область применения

1.1 This test method describes an accelerated procedure for determining comparative characteristics of coating systems applied to the exterior of steel pipe for the purpose of preventing or mitigating corrosion that may occur in underground or immersion where the pipe is carrying heated media and is under cathodic protection. This test method is intended for use with samples of coated pipe, or with a specimen cut from the section of coated pipe or flat plates, and is applicable to such samples when the coating is characterized by function as an electrical barrier.

1.2 This test method is intended to simulate conditions when external coatings are exposed to high temperature inside the pipe and to an ambient temperature outside, and thus are subjected to temperature gradient. If elevated temperatures are not required, see Test Method G8. If a specific test method is required with no options, see Test Method G80. If elevated temperatures are required but without temperature gradient, see Test Method G42.

1.3 The values stated in SI units to three significant decimals are to be regarded as the standard. The values given in parentheses are for information only.

1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

Ключевые слова:
cathodic disbondment; elevated temperature; pipeline coatings