ASTM D731-18
Standard Test Method for Molding Index of Thermosetting Molding Powder
4 стр.
Заменен
Электронный (pdf)Печатное издание
87.36 $ (включая НДС 20%)
Разработчик:
Зарубежные/ASTM
ICS:
83.080.10 Thermosetting. Including ebonite / Термореактивные материалы
Сборник (ASTM):
08.01 Plastics (I): C1147–D3159 / Пластмасса (I): C1147–D3159
Тематика:
Plastics
Описание
Значение и использование

5.1 This test method provides a guide for evaluating the moldability of thermosetting molding powders. This test method does not necessarily denote that the molding behavior of different materials will be alike and trials may be necessary to establish the appropriate molding index for each material in question.

5.2 The sensitivity of this test diminishes when the molding pressure is decreased below 5.3 MPa (764 psi), so pressures lower than this are not ordinarily recommended. This is due to the friction of moving parts and the insensitivity of the pressure switch actuating the timer at these low pressures.

Область применения

1.1 This test method covers the measurement of the molding index (plasticity) of thermosetting plastics ranging in flow from soft to stiff by selection of appropriate molding pressures within the range from 3.7 to 36.5 MPa (530 to 5300 psi).

1.2 The values stated in SI units are to be regarded as the standard. The values given in parentheses are for information only.

1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.

1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

Ключевые слова:
molding index; plasticity; thermosets;