An electrical pulse is applied to a piezoelectric transducer which converts electrical to mechanical energy. In the angle-beam search unit, the piezoelectric element is generally a thickness expander which creates compressions and rarefactions. This longitudinal (compressional) wave travels through a wedge (generally a plastic). The angle between transducer face and the examination face of the wedge is equal to the angle between the normal (perpendicular) to the examination surface and the incident beam. Fig. 1 shows the incident angle ϕ_i, and the refracted angle ϕ_r, of the ultrasonic beam.

When the examination face of the angle-beam search unit is coupled to a material, ultrasonic waves may travel in the material. As shown in Fig. 2, the angle in the material (measured from the normal to the examination surface) and mode of vibration are dependent on the wedge angle, the ultrasonic velocity in the wedge, and the velocity of the wave in the examined material. When the material is thicker than a few wavelengths, the waves traveling in the material may be longitudinal and shear, shear alone, shear and Rayleigh, or Rayleigh alone. Total reflection may occur at the interface. (Refer to Fig. 3.) In thin materials (up to a few wavelengths thick), the waves from the angle-beam search unit traveling in the material may propagate in different Lamb wave modes.

All ultrasonic modes of vibration may be used for angle-beam examination of material. The material forms and the probable flaw locations and orientations determine selection of beam directions and modes of vibration. The use of angle beams and the selection of the proper wave mode presuppose a knowledge of the geometry of the object; the probable location, size, orientation, and reflectivity of the expected flaws; and the laws of physics governing the propagation of ultrasonic waves. Characteristics of the examination system used and the ultrasonic properties of the material being examined must be known or determined. Some materials, because of unique microstructure, are difficult to examine using ultrasonics. Austenitic material, particularly weld material, is one example of this material condition. Caution should be exercised when establishing examination practices for these type materials. While examination may be possible, sensitivity will be inferior to that achievable on ferritic materials. When examining materials with unique microstructures, empirical testing should be performed to assure that the examination will achieve the desired sensitivity. This may be accomplished by incorporating known reflectors in a mock up of the weld or part to be examined.

Angle-Beam Longitudinal Waves—As shown in Fig. 4, angle-beam longitudinal waves with refracted angles in the range from 1 to 40° (where coexisting angle-beam shear waves are weak, as shown in Fig. 3) may be used to detect fatigue cracks in axles and shafts from the end by direct reflection or by corner reflection. As shown in Fig. 5, with a crossed-beam dual-transducer search unit configuration, angle-beam longitudinal waves may be used to measure thickness or to detect reflectors parallel to the examination surface, such as laminations. As shown in Fig. 6, reflectors with a major plane at an angle up to 40° with respect to the examination surface, provide optimum reflection to an angle-beam longitudinal wave that is normal to the plane of the reflector. Angle-beam longitudinal waves in the range from 45 to 85° become weaker as the angle increases; at the same time, the coexisting angle-beam shear waves become stronger. Equal amplitude angle beams of approximately 55° longitudinal wave and 29° shear wave will coexist in the material, as shown in Fig. 7. Confusion created by two beams traveling at different angles and at different velocities has limited use of this range of angle beams.

Angle-Beam Shear Waves (Transverse Waves)—Angle-beam shear waves in the range from 40 to 75° are the most used angle beams. They will detect imperfections in materials by corner reflection and reradiation (as shown in Fig. 8) if the plane of the reflector is perpendicular to a material surface, and by direct reflection if the ultrasonic beam is normal to the plane of the reflector (as shown in Fig. 9). Reflectors parallel to the examination surface (such as laminations in plate, as shown in Fig. 10) can rarely be detected by an angle beam unless accompanied by another reflector; for example, a lamination at the edge of a plate (as shown in Fig. 11) can be detected by corner reflection from the lamination and plate edge. Generally, laminations should be detected and evaluated by the straight-beam technique. Angle-beam shear waves applied to weld testing will detect incomplete penetration (as shown in Fig. 12) by corner reflection, incomplete fusion (as shown in Fig. 13) by direct reflection (when the beam angle is chosen to be normal to the plane of the weld preparation), slag inclusion by cylindrical reflection (as shown in Fig. 14), porosity by spherical reflection, and cracks (as shown in Fig. 15) by direct or corner reflection, depending on their orientation. Angle-beam shear waves of 80 to 85° are frequently accompanied by a Rayleigh wave traveling on the surface. Confusion created by two beams at slightly different angles, traveling at different velocities, has limited applications in this range of angle beams.

Surface-Beam Rayleigh Waves—Surface-beam Rayleigh waves travel at 90° to the normal of the examination surface on the examination surface. In material greater than two wavelengths thick, the energy of the Rayleigh wave penetrates to a depth of approximately one wavelength; but, due to the exponential distribution of the energy, one half of the energy is within one-quarter wavelength of the surface. Surface cracks with length perpendicular to the Rayleigh wave can be detected and their depth evaluated by changing the frequency of the Rayleigh wave, thus changing its wavelength and depth of penetration. Wavelength equals velocity divided by frequency.
Область применения

1.1 This practice covers ultrasonic examination of materials by the pulse-echo technique, using continuous coupling of angular incident ultrasonic vibrations.

1.2 This practice shall be applicable to development of an examination procedure agreed upon by the users of the practice.

1.3 The values stated in inch-pound units are regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.

1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.