This International Standard describes a test method that covers the determination of fracture toughness of monolithic ceramic materials at room temperature by the surface crack in flexure (SCF) method.
This International Standard is intended for use with monolithic ceramics and whisker- or particulate-reinforced ceramics that are regarded as macroscopically homogeneous. It does not include continuous-fibre reinforced ceramic composites.
The test method is applicable to materials with either flat or rising crack growth resistance curves. This method is similar to ISO 15732 except that precracks are smaller and are made by a different procedure. The methods should produce similar or identical results for materials with a flat R-curve.
NOTE This test method is usually applicable to ceramic materials with a fracture toughness less than 10 MPa m1/2. It may be difficult to form precracks with a Knoop indenter for materials with greater fracture toughness or those materials which are soft (low hardness) such as some zirconias, or for porous ceramics.
Diese Internationale Norm legt ein Prüfverfahren zur Bestimmung der Bruchzähigkeit monolithischer keramischer Werkstoffe fest, das bei Raumtemperatur an Biegeproben mit Oberflächenriss (Knoop-Riss) (SCF-Verfahren) durchgeführt wird. Diese Internationale Norm ist für die Anwendung auf monolithische Keramiken und durch Whisker oder Teilchen verstärkte Keramiken vorgesehen, die makroskopisch als homogen angesehen werden. Keramische Verbundstoffe mit Endlosfaserverstärkung werden nicht erfasst. Das Prüfverfahren ist auf keramische Werkstoffe mit flachen oder ansteigenden Risswiderstandskurven (R-Kurven) anwendbar. Es ist mit dem in ISO 15732 festgelegten Verfahren vergleichbar, allerdings sind die Anrisse kleiner und werden auf andere Weise erzeugt. Beide Verfahren sollten für Werkstoffe mit flacher Risswiderstandskurve ähnliche oder identische Ergebnisse liefern.