This specification covers nickel-iron-chromium-molybdenum-columbium stabilized alloy (UNS N08700) bar. The final treatment of the material shall be a solution anneal. Straightening or cold finishing, or both, may be performed after the final solution annealing operation. Cold drawing to more than a minor sizing reduction after the final solution annealing is not recommended. Heat analysis shall conform to the requirements as to chemical composition prescribed. Tensile strength, yield strength, and elongation shall conform to the mechanical property requirements of the material as set by this specification. Test methods such as corrosion test, chemical analysis, tension test, and rounding procedure test shall be carried out.
Область применения1.1 This specification covers nickel-iron-chromium-molybdenum-columbium stabilized alloy (UNS N08700)2 bar.
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to become familiar with all hazards including those identified in the appropriate Safety Data Sheet (SDS) for this product/material as provided by the manufacturer, to establish appropriate safety, health, and environmental practices, and determine the applicability of regulatory limitations prior to use.
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.