This specification covers the chemical, mechanical, and dimensional requirements, and associated test methods for steel rivets for use in boilers and pressure vessels, and steel bars for use in the manufacture of such rivets. Two grades of steel are covered here, as follows: Grade A and Grade B. The steel used to make the rivets shall be manufactured by open-hearth, electric-furnace, or basic-oxygen process, and the corresponding rivets shall be manufactured from steel bars conforming to the applicable bar grade ordered. The steel shall undergo heat and product analysis for measurements of chemical contents for carbon, manganese, phosphorus, and sulfur. Finished bars and rivets shall go through rivet bend, rivet flattening, bar tensile, and bar bend tests for measurements of mechanical properties such as ratio of bend diameter to diameter of the shank for rivets, and tensile strength, yield point, elongation, and ratio of bend diameter to diameter of specimen for bars.

1.1 This specification2 covers steel rivets for use in boilers and pressure vessels and steel bars for use in the manufacture of rivets.

1.2 Two grades are covered:

1.2.1 Grade A—Bars having a yield point of 23 000 psi (160 MPa) minimum with carbon 0.18 % maximum.

1.2.2 Grade B—Bars having a yield point of 29 000 psi (200 MPa) minimum with carbon 0.28 % maximum.

1.2.3 Rivets are manufactured from the applicable bar grade.

1.3 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.

1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.