This specification covers austenitic gray iron castings that are used primarily for their resistance to heat, corrosion, and wear. The types of castings covered here are: Type 1, Type 1b, Type 2, Type 2b, Type 3, Type 4, Type 5, and Type 6. The materials shall be manufactured by melting in any furnace that produces castings which includes cupolas, air furnaces, electric furnaces, crucible furnaces, and so forth. Heat and product analyses shall be performed wherein specimens shall conform to required chemical composition of carbon, silicon, manganese, nickel, copper, chromium, sulfur, and molybdenum. The materials shall undergo a nonmagnetic test which is based on the material's attraction to a small steel horseshoe-type magnet and a magnetic permeability test in the event that nonmagnetic castings are specified. Tension tests shall be performed wherein specimens shall conform to required tensile strength and Brinell hardness.

1.1 This specification covers austenitic gray iron castings that are used primarily for their resistance to heat, corrosion, and wear. Austenitic gray iron is characterized by uniformly distributed graphite flakes, some carbides, and the presence of sufficient alloy content to produce an austenitic structure.

1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.

1.3 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.