This specification covers vacuum-treated alloy steel forgings intended for use as turbine rotor disks and wheels. The steel shall be made by the basic electric-furnace process. The molten steel shall be vacuum treated using either the vacuum stream degassing process, vacuum-lift process or ladle degassing process prior to or during the pouring of the ingot in order to remove objectionable gases, particularly hydrogen. The forgings shall receive their hot mechanical work under a press, hammer, or mill of sufficient power to work the metal throughout its section. Before reheating for heat treatment, the forging shall be allowed to cool in a manner to prevent damage and to accomplish transformation. The forgings shall be heated to a suitable temperature for a sufficient length of time for complete austenitization and shall be tempered to develop the specified properties. The forgings shall be preliminarily machined on all surfaces prior to heat treatment and shall be stress relieved after machining. To measure some mechanical properties, the specimens shall be subjected to tension test, impact test, and hardness test. A non-destructive test like an ultrasonic inspection shall be made on all available surfaces to demonstrate freedom from detrimental internal indications.

1.1 This specification covers vacuum-treated alloy steel forgings intended for use as turbine rotor disks and wheels.

1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.

1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.