Реферат

This specification covers the standard for heat-treated carbon manganese-silicon steel plates intended for fusion welded pressure vessels and structures. The steel shall be killed and undergo normalization, quenching and tempering. Heat and product analyses shall be performed on the materials and results shall conform to the required values in chemical composition in carbon, manganese, phosphorus, sulfur, silicon, copper, nickel, chromium and molybdenum. Mechanical testing like tension test shall be done on the plates and shall conform to the required tensile strength, yield strength, and elongation.

Область применения

1.1 This specification covers heat-treated carbon-manganese-silicon steel plates intended for fusion welded pressure vessels and structures.

1.2 Plates furnished under this specification are available in the following three classes:

Yield Tensile Strength, Strength, Heat Thickness, min, ksimin, ksi Class Treatment [MPa][MPa] 1
Normalized
2½ in. and
under
[65 mm and
under]
50

[345]
70

[485]
Over 2½ to 4 in.
[Over 65 to 100
mm]
45
[310]
65
[450]
2
Quenched
and tempered
2½ in. and
under
[65 mm and
under]
60

[415]
80

[550]
Over 2½ to 4 in.
[Over 65 to 100
mm]
55
[380]
75
[515]
Over 4 to 6 in.
[Over 100 to 150
mm]
46
[315]
70
[485]
3
Quenched
and tempered
2½ in. and
under
[65 mm and
under]
55

[380]
80

[550]
Over 2½ to 4 in.
[Over 65 to 100
mm]
50
[345]
75
[515]
Over 4 to 6 in.
[Over 100 to 150
mm]
40
[275]
70
[485]

1.3 The maximum thickness of plates furnished under this specification is 4 in. [100 mm] for Class 1 and 6 in. [150 mm] for Class 2 and Class 3.

1.4 The values stated in either inch-pound units or SI units are to be regarded separately as standard. Within the text, the SI units are shown in brackets. The values stated in each system are not exact equivalents; therefore, each system is to be used independently of the other without combining values in any way.