ASTM A852/A852M-03(2007)

Отменен
Standard Specification for Quenched and Tempered Low-Alloy Structural Steel Plate with 70 ksi [485 MPa] Minimum Yield Strength to 4 in. [100 mm] Thick (Withdrawn 2010) — 3 стр.
Причина отмены

This specification covers quenched and tempered high-strength low-alloy structural steel plates for welded, riveted, or bolted construction.

Formerly under the jurisdiction of Committee A01 on Steel, Stainless Steel and Related Alloys, this specification was withdrawn in October 2010. This standard was withdrawn without replacement due to its limited use by the industry.

Реферат

This specification covers quenched and tempered high-strength low-alloy structural steel plates for welded, riveted, or bolted construction. It is intended primarily for use in welded bridges and buildings where savings in weight, added durability, and good notch toughness are important. When properly exposed to the atmosphere, this steel can be used bare (unpainted) for many applications. The steel shall conform on heat and product analysis to the chemical composition requirements prescribed for carbon, manganese, phosphorus, sulfur, silicon, nickel, chromium, copper, and vanadium. Tensile test requirements shall include: yield strength, tensile strength, and elongation. The requirements for manufacturing, heat treatment, and longitudinal Charpy V-notch impact testing are given as well.

Область применения

1.1 This specification covers quenched and tempered high-strength low-alloy structural steel plates for welded, riveted, or bolted construction. It is intended primarily for use in welded bridges and buildings where savings in weight, added durability, and good notch toughness are important. The atmospheric corrosion resistance of this steel in most environments is substantially better than that of carbon structural steels with or without copper addition (see Note 1). When properly exposed to the atmosphere, this steel can be used bare (unpainted) for many applications. Welding technique is of fundamental importance, and it is presupposed that the welding procedure will be suitable for the steel and the intended service. This specification is limited to material up to 4 in. [100 mm], inclusive, in thickness. See Appendix X3 of Specification A 6/A 6M for information on weldability. Note 1—For methods of estimating the atmospheric corrosion resistance of low-alloy steels, see Guide G 101.

1.2 Plates produced under this specification are impact tested at a temperature not higher than 50°F [10°C].

1.3 The values stated in inch-pound units or SI units are to be regarded separately as standard. Within the text, the SI units are shown in brackets. The values stated in each item are not exact equivalents. Therefore, each system must be used independently of the other. Combining values from the two systems may result in nonconformance with this specification.

ICS
77.140.50 Flat. Including plate, sheet and strip / Стальной листовой прокат и полуфабрикаты. Включая плиты, листы и полосы
Сборник ASTM
01.04 Steel--Structural, Reinforcing, Pressure Vessel, Railway / Сталь - Конструкционная, арматурная, для сосудов под давлением, рельсовая
Тематика
Steel--Structural, Tubes, Plate, Coated