This specification covers the magnetic property requirements of 50 nickel-50 iron soft magnetic parts fabricated by powder metallurgy techniques in the sintered or annealed conditions, intended for parts that require high magnetic permeability, high electrical resistivity, low coercive field strength, and low hysteresis loss. This specification does not cover parts produced by metal injection molding. Parts shall be tested and adhere to the chemical composition, sintered density and coercive field strength requirements listed in this specification. Appendices contain information on typical magnetic properties and heat treatment.

1.1 This specification covers the magnetic properties of 50 nickel-50 iron parts fabricated by powder metallurgy techniques and is intended for parts that require high magnetic permeability, high electrical resistivity, low coercive field strength, and low hysteresis loss. It differs from the wrought alloy specification (see Specification A753) because these parts are porous. A number of magnetic properties such as permeability are proportional to the sintered density.

1.2 This specification deals with powder metallurgy parts in the sintered or annealed condition. Should the sintered parts be subjected to any secondary operation that causes mechanical strain, such as machining or sizing, they should be resintered or annealed.

1.3 The values stated in customary (cgs-emu and inch-pound) units are to be regarded separately as standard. The values given in parentheses are mathematical conversions to SI units, which are provided for information only and are not considered standard.