Реферат

This specification covers rolled or cold-finished aluminum and aluminum-alloy bar, rod, and wire and includes the following UNS alloy designations: A91060, A91100, A92011, A92014, A92017, A92024, A92219, A93003, A95052, A95056, A95154, A96061, A96110, A96262, and A97075. The temper conditions covered by this specification include: O, H14, H18, H12, H16, H112, F, T3, T4, T42, T451, T6, T62, T651, T36, T351, T851, H32, H34, H36, H38, H111, H192, H392, T 89, T94, T9, T73, and T7351. The products shall be produced either by hot extruding and cold finishing or by hot rolling with or without cold finishing. Bars, rods, and wires shall conform to the chemical composition requirements prescribed for aluminum, silicon, iron, copper, manganese, magnesium, chromium, zinc, bismuth, lead, and titanium, and to the specified tensile properties such as tensile strength, yield strength, and elongation. Requirements for quality assurance, heat treatment, chemical analysis, tension test, heat-treat response, bend testing, and stress-corrosion resistance and stress-corrosion cracking test are detailed.

Область применения

1.1 This specification covers rolled or cold-finished bar, rod, and wire in alloys (Note 1) and tempers as shown in Table 2.

Note 1—Throughout this specification use of the term alloy in the general sense includes aluminum as well as aluminum alloy.

Note 2—The term cold finished is used to indicate the type of surface finish, sharpness of angles, and dimensional tolerances produced by drawing through a die.

Note 3—See Specification B221 for aluminum and aluminum-alloy extruded bars, rods, wire, shapes, and tubes; and Specification B316/B316M for aluminum and aluminum-alloy rivet and cold-heading wire and rods.

1.2 Alloy and temper designations are in accordance with ANSI H35.1. The equivalent UNS alloy designations are those of Table 1 preceded by A9, for example, A91100 for aluminum 1100 in accordance with Practice E527.

1.3 A complete metric companion to Specification B211 has been developedB211M; therefore, no metric equivalents are presented in this specification.

1.4 For acceptance criteria for inclusion of new aluminum and aluminum alloys in this specification, see Annex A2.

TABLE 1 Chemical Composition Limits^A,B,C,D

AlloySiFeCuMnMgCrNiZnTiBiPbSnOther Elements^EAluminum EachTotal^F 11000.95 Si + Fe0.05–0.200.05.........0.10............0.050.15 99.00 min^G 20110.400.75.0–6.0............0.30...0.20–0.60.20–0.6...0.050.15remainder 20140.50–1.20.73.9–5.00.40–1.20.20–0.80.10...0.25.........0.150.050.15remainder 20170.20–0.80.73.5–4.50.40–1.00.40–0.80.10...0.25.........0.150.050.15remainder 20240.500.503.8–4.90.30–0.91.2–1.80.10...0.25.........0.150.050.15remainder 22190.200.305.8–6.80.20–0.400.02......0.10.........0.02–0.100.05^H0.15^Hremainder 30030.60.70.05–0.201.0–1.5.........0.10............0.050.15remainder 403211.0–13.51.00.50–1.3...0.8–1.30.100.5–1.30.25............0.050.15remainder 50520.250.400.100.102.2–2.80.15–0.35...0.10............0.050.15remainder 50560.300.400.100.05–0.204.5–5.60.05–0.20...0.10............0.050.15remainder 5154^I0.250.400.100.103.1–3.90.15–0.35...0.20.........0.200.050.15remainder 60130.6–1.00.500.6–1.10.20–0.80.8–1.20.10...0.250.10.........0.050.15remainder 60200.40–0.90.500.30–0.90.350.6–1.20.15...0.200.15...0.050.9–1.50.050.15remainder 60610.40–0.80.70.15–0.400.150.8–1.20.04–0.35...0.25.........0.150.050.15remainder 61100.7–1.50.80.20–0.70.20–0.70.50–1.10.04–0.25...0.30.........0.150.050.15remainder 62620.40–0.80.70.15–0.400.150.8–1.20.04–0.14...0.25...0.40–0.70.40–0.70.150.050.15remainder 70750.400.501.2–2.00.302.1–2.90.18–0.28...5.1–6.1.........0.200.050.15remainder

^A Limits are in mass percent maximum unless otherwise shown.

^B Analysis shall be made for the elements for which limits are shown in this table.

^C For purposes of determining conformance to these limits, an observed value or a calculated value obtained from analysis shall be rounded to the nearest unit in the last right-hand place of figures used in expressing the specified limit, in accordance with the rounding-off method of Practice E29.

^D In case of any discrepancy in the values listed in Table 3 when compared with those listed in the “Teal Sheets” (International Alloy Designations and Chemical Composition Limits for Wrought Aluminum and Wrought Aluminum Alloys), the composition limits registered with The Aluminum Association and published in the “Teal Sheets” shall be considered the controlling composition.

^E Others includes listed elements for which no specific limit is shown as well as unlisted metallic elements. The producer may analyze samples for trace elements not specified in the specification. However, such analysis is not required and may not cover all metallic Others elements. Should any analysis by the producer or the purchaser establish that an Others element exceeds the limit of Each or that the aggregate of several Others elements exceeds the limit of Total, the material shall be considered non-conforming.

^F Other elementsTotal shall be the sum of unspecified metallic elements 0.010 % or more each, rounded to the second decimal before determining the sum.

^G The aluminum content is the difference between 100.00 % and the sum of all other metallic elements and silicon present in amounts of 0.010 % or more each, rounded to the second decimal before determining the sum.

^H Vanadium 0.05–0.15 % zirconium 0.10–0.25 %. The total for other elements does not include vanadium and zirconium.

^I Beryllium 0.0003 maximum for welding electrode and welding rod only.