Область применения

1.1 This specification covers aluminum and aluminum-alloy extruded bars, rods, wires, profiles, and tubes in the aluminum alloys (Note 1) and tempers shown in Table 2.

TABLE 1 Chemical Composition Limits ^A,B,CNote 1—In case of a discrepancy between the values listed in Table 1 and those listed in the “International Alloy Designations and Chemical Composition Limits for Wrought Aluminum and Wrought Aluminum Alloys”(known as the “Teal Sheets”), the composition limits registered with the Aluminum Association and published in the “Teal Sheets” should be considered the controlling composition. The “Teal Sheets” are available at http://www.aluminum.org/tealsheets.

Alloy

Silicon

Iron

Copper

Manga-
nese

Magne-
sium

Chromium

Zinc

Titanium

Vanadium

Other Elements^D

Aluminum

Each

Total^E

1060

0.25

0.35

0.05

0.03

0.03

...

0.05

0.03

0.05

0.03

...

99.60 min^F

1100

0.95 Si + Fe

0.05–0.20

0.05

...

...

0.10

...

...

0.05^G

0.15

99.00 min^F

2014

0.50–1.2

0.7

3.9–5.0

0.40–1.2

0.20–0.8

0.10

0.25

0.15^H

...

0.05^H

0.15

remainder

2024

0.50

0.50

3.8–4.9

0.30–0.9

1.2–1.8

0.10

0.25

0.15^H

...

0.05^H

0.15

remainder

2219

0.20

0.30

5.8–6.8

0.20–0.40

0.02

...

0.10

0.02–0.10

0.05–0.15

0.05^I

0.15^I

remainder

3003

0.6

0.7

0.05–0.20

1.0–1.5

...

...

0.10

...

...

0.05

0.15

remainder

Alclad 3003

...

3003 Clad with 7072 alloy

...

...

...

...

...

...

...

...

3004

0.30

0.7

0.25

1.0–1.5

0.8–1.3

...

0.25

...

...

0.05

0.15

remainder

3102

0.40

0.7

0.10

0.05–0.40

...

...

0.30

0.10

...

0.05

0.15

remainder

5052

0.25

0.40

0.10

0.10

2.2–2.8

0.15–0.35

0.10

...

...

0.05

0.15

remainder

5083

0.40

0.40

0.10

0.40–1.0

4.0–4.9

0.05–0.25

0.25

0.15

...

0.05

0.15

remainder

5086

0.40

0.50

0.10

0.20–0.7

3.5–4.5

0.05–0.25

0.25

0.15

...

0.05

0.15

remainder

5154

0.25

0.40

0.10

0.10

3.1–3.9

0.15–0.35

0.20

0.20

...

0.05

0.15

remainder

5454

0.25

0.40

0.10

0.50–1.0

2.4–3.0

0.05–0.20

0.25

0.20

...

0.05

0.15

remainder

5456

0.25

0.40

0.10

0.50–1.0

4.7–5.5

0.05–0.20

0.25

0.20

...

0.05

0.15

remainder

6005

0.6–0.9

0.35

0.10

0.10

0.40–0.6

0.10

0.10

0.10

...

0.05

0.15

remainder

6005A

0.50–0.9

0.35

0.30

0.50^J

0.40–0.7

0.30^J

0.20

0.10

...

0.05

0.15

remainder

6013

0.6-1.0

0.50

0.6-1.1

0.20-0.8

0.8-1.2

0.10

0.25

0.10

…

0.05

0.15

remainder

6020^K

0.40–0.9

0.50

0.30–0.9

0.35

0.6–1.2

0.15

0.20

0.15

...

0.05

0.15

remainder

6041^L

0.50–0.9

0.15–0.7

0.15–0.6

0.05–0.20

0.8–1.2

0.05–0.15

0.25

0.15

...

0.05

0.15

remainder

6042^M

0.50–1.2

0.7

0.20–0.6

0.40

0.7–1.2

0.04–0.35

0.25

0.15

...

0.05

0.15

remainder

6060

0.30–0.6

0.10–0.30

0.10

0.10

0.35–0.6

0.5

0.15

0.10

...

0.05

0.15

remainder

6061^N

0.40–0.8

0.7

0.15–0.40

0.15

0.8–1.2

0.04–0.35

0.25

0.15

...

0.05

0.15

remainder

6063

0.20–0.6

0.35

0.10

0.10

0.45–0.9

0.10

0.10

0.10

...

0.05

0.15

remainder

6064^O

0.40–0.8

0.7

0.15–0.40

0.15

0.8–1.2

0.05–0.14

0.25

0.15

...

0.05

0.15

remainder

6066

0.9–1.8

0.50

0.7–1.2

0.6–1.1

0.8–1.4

0.40

0.25

0.20

...

0.05

0.15

remainder

6070

1.0–1.7

0.50

0.15–0.40

0.40–1.0

0.50–1.2

0.10

0.25

0.15

...

0.05

0.15

remainder

6082

0.7–1.3

0.50

0.10

0.40–1.0

0.6–1.2

0.25

0.20

0.10

...

0.05

0.15

remainder

6105

0.6–1.0

0.35

0.10

0.15

0.45–0.8

0.10

0.10

0.10

...

0.05

0.15

remainder

6162

0.40–0.8

0.50

0.20

0.10

0.7–1.1

0.10

0.25

0.10

...

0.05

0.15

remainder

6262

0.40–0.8

0.7

0.15–0.40

0.15

0.8–1.2

0.04–0.14

0.25

0.15

...

0.05^P

0.15^P

remainder

6351

0.7–1.3

0.50

0.10

0.40–0.8

0.40–0.8

...

0.20

0.20

...

0.05

0.15

remainder

6360

0.35–0.8

0.10–0.30

0.15

0.02–0.15

0.25–0.45

0.05

0.10

0.10

...

0.05

0.15

remainder

6463

0.20–0.6

0.15

0.20

0.05

0.45–0.9

...

0.05

...

...

0.05

0.15

remainder

6560

0.30–0.7

0.10–0.30

0.05–0.20

0.20

0.20–0.6

0.05

0.15

0.10

...

0.05

0.15

remainder

7005

0.35

0.40

0.10

0.20–0.7

1.0–1.8

0.06–0.20

4.0–5.0

0.01–0.06

...

0.05^Q

0.15^Q

remainder

7072^R

0.7 Si + Fe

0.10

0.10

0.10

...

0.8–1.3

...

...

 

 

remainder

7075

0.40

0.50

1.2–2.0

0.30

2.1–2.9

0.18–0.28

5.1–6.1

0.20^S

...

0.05^S

0.15

remainder

7116

0.15

0.30

0.50–1.1

0.05

0.8–1.4

...

4.2–5.2

0.05

0.05

0.05^T

0.15

remainder

7129

0.15

0.30

0.50–0.9

0.10

1.3–2.0

0.10

4.2–5.2

0.05

0.05

0.05^T

0.15

remainder

7178

0.40

0.50

1.6–2.4

0.30

2.4–3.1

0.18–0.28

6.3–7.3

0.20

...

0.05

0.15

remainder

^A Limits are in weight percent maximum unless shown as a range, or stated otherwise.^B Analysis shall be made for the elements for which limits are shown in this table.^C For the purpose of determining conformance to these limits, an observed value or a calculated value obtained from analysis shall be rounded to the nearest unit in the last right-hand place of the figures used in expressing the specified limit, in accordance with the rounding-off method of Practice E29.^D Others includes listed elements for which no specific limit is shown as well as unlisted metallic elements. The producer may analyze samples for trace elements not specified in the specification. However, such analysis is not required and may not cover all metallic Others elements. Should any analysis by the producer or the purchaser establish that an Others element exceeds the limit of Each or that the aggregate of several Others elements exceeds the limit of Total, the material shall be considered nonconforming.^E Other Elements—Total shall be the sum of unspecified metallic elements 0.010 % or more, rounded to the second decimal before determining the sum.^F The aluminum content shall be calculated by subtracting from 100.00 % the sum of all metallic elements present in amounts of 0.010 % or more each, rounded to the second decimal before determining the sum.^G Be 0.0003 max for welding electrode, welding rod, and filler wire.^H Upon agreement between the purchaser and the producer or supplier, a Zr + Ti limit of 0.20 % max is permitted. Properties in Specification (Table 2) are not based on the Zirconium and Titanium algorithm.^I Zirconium, 0.10–0.25 %. The total for other elements does not include zirconium.^J Manganese plus chromium shall total 0.12–0.50.^K Lead 0.05 % max, Tin 0.9-1.5 %.^L Bismuth 0.30-0.9 %, Tin 0.35-1.2 %.^M Bismuth 0.20-0.8 % Lead 0.15-0.40 %.^N In 1965 the requirements for 6062 were combined with those for 6061 by revising the minimum chromium from “0.15 %” to“ 0.04 %.” This action cancelled alloy 6062.^O Bismuth 0.50-0.7 %, Lead 0.20-.040 %,^P Bismuth and lead shall be 0.40–0.7 % each.^Q Zirconium 0.08–0.20 %. The total for other elements does not include zirconium. ^R Composition of cladding alloy applied during the course of manufacture. Samples from finished tube shall not be required to conform to these limits.^S Upon agreement between the purchaser and the producer or supplier, a Zr + Ti limit of 0.25 % max is permitted. Properties in Specification (Table 2) are not based on the Zirconium and Titanium algorithm.^T Gallium 0.03 % max.TABLE 2 Tensile Property Limits^A,B

Temper

 

Specified Section or Wall Thickness, mm

Area, mm²

Tensile Strength, MPa

Yield Strength (0.2 % offset), MPa

Elongation,^C %, min

 

 

over

incl

over

incl

min

max

min

max

in 50 mm

in 5 ×
Diameter

Aluminum 1060

O

 

 

all

 

all

 

60

95

15

. . .

25

22

H112

 

 

all

 

all

 

60

. . .

15

. . .

25

22

F^D

 

 

all

 

all

 

. . .

. . .

. . .

. . .

. . .

. . .

Aluminum 1100

O

 

 

all

 

all

 

75

105

20

. . .

25

22

H112

 

 

all

 

all

 

75

. . .

20

. . .

25

22

F^D

 

 

all

 

all

 

. . .

. . .

. . .

. . .

. . .

. . .

Alloy 2014

O

 

 

all

 

all

 

. . .

205

. . .

125

12

10

T4

 

all

 

all

 

345

. . .

240

. . .

12

10

T4510^E

 

 

 

 

 

 

 

 

 

 

 

T4511^E

 

 

 

 

 

 

 

 

 

 

 

T42^F

 

 

all

 

all

 

345

. . .

200

. . .

12

10

T6

. . .

12.50

all

 

415

. . .

365

. . .

7

6

T6510^E

12.50

18.00

all

 

440

. . .

400

. . .

. . .

6

T6511^E

18.00

. . .

. . .

16 000

470

. . .

415

. . .

. . .

6

 

 

18.00

. . .

16 000

20 000

470

. . .

400

. . .

. . .

5

T62^F

 

. . .

18.00

all

. . .

415

. . .

365

. . .

7

6

 

 

18.00

. . .

. . .

16 000

415

. . .

365

. . .

. . .

6

 

 

18.00

. . .

16 000

20 000

415

. . .

365

. . .

. . .

5

F^D

 

 

all

 

all

. . .

. . .

. . .

. . .

. . .

. . .

. . .

Alloy 2024

O

 

 

all

 

all

 

. . .

240

. . .

130

12

10

T3

 

. . .

6.30

all

 

395

. . .

290

. . .

12^G

. . .

T3510^E

 6.30

18.00

all

 

415

. . .

305

. . .

12^G

10^G

T3511^E

18.00

35.00

all

 

450

. . .

315

. . .

. . .

9

 

 

35.00

. . .

. . .

16 000

485

. . .

360^H

. . .

. . .

9

 

 

35.00

. . .

16 000

20 000

470

. . .

330^I

. . .

. . .

7

T42^F

 

. . .

18.00

all

. . .

395

. . .

260

. . .

12

10

 

 

18.00

35.00

all

 

395

. . .

260

. . .

. . .

9

 

 

35.00

. . .

. . .

16 000

395

. . .

260

. . .

. . .

9

 

 

35.00

. . .

16 000

20 000

395

. . .

260

. . .

. . .

7

T81

 1.20

6.30

all

 

440

. . .

385

. . .

4

. . .

T8510^E

 6.30

35.00

all

 

455

. . .

400

. . .

5

4

T8511^E

35.00

. . .

. . .

20 000

455

. . .

400

. . .

. . .

4

F^D

 

 

all

 

all

 

. . .

. . .

. . .

. . .

. . .

. . .

Alloy 2219

O

 

 

all

 

all

 

. . .

220

. . .

125

12

10

T31

. . .

12.50

. . .

16 000

290

. . .

180

. . .

14

12

T3510^E

12.50

80.00

 

16 000

310

. . .

185

. . .

. . .

12

T62^F

. . .

25.00

. . .

16 000

370

. . .

250

. . .

6

5

 

 

25.00

 

. . .

20 000

370

. . .

250

. . .

. . .

5

T81

 

 

 

 

 

 

 

 

 

 

 

T8510^E

 

. . .

80.00

. . .

16 000

400

. . .

290

. . .

6

5

T8511^E

 

 

 

 

 

 

 

 

 

 

 

F^D

 

 

all

 

all

 

. . .

. . .

. . .

. . .

. . .

. . .

Alloy 3003

O

 

 

all

 

all

 

95

130

35

. . .

25

22

H112

 

 

all

 

all

 

95

. . .

35

. . .

25

22

F^D

 

 

all

 

all

 

. . .

. . .

. . .

. . .

. . .

. . .

Alclad Alloy 3003

O

 

 

all

all

all

 

90

125

30

. . .

25

. . .

H112

 

 

all

 

 

 

90

. . .

30^J

. . .

25

. . .

Alloy 3004

O

 

 

all

 

all

 

160

200

60

. . .

. . .

. . .

F^D

 

 

all

 

all

 

. . .

. . .

. . .

. . .

. . .

. . .

Alloy 3102

H112^K

 

 

 0.70

1.30

all

 

75

125

30

. . .

25

. . .

Alloy 5052

O

 

 

all

 

all

 

170

240

70

. . .

. . .

. . .

Alloy 5083

O

 

 

. . .

130.00^L

. . .

20 000

270

350

110

. . .

14

12

H111

 

 

. . .

130.00^L

. . .

20 000

275

. . .

165

. . .

12

10

H112

 

 

. . .

130.00^L

. . .

20 000

270

. . .

110

. . .

12

10

F^D

 

 

all

 

all

 

. . .

. . .

. . .

. . .

. . .

. . .

Alloy 5086

O

 

 

. . .

130.00^L

. . .

20 000

240

315

95

. . .

14

12

H111

 

 

. . .

130.00^L

. . .

20 000

250

. . .

145

. . .

12

10

H112

 

 

. . .

130.00^L

. . .

20 000

240

. . .

95

. . .

12

10

F^D

 

 

all

 

all

 

. . .

. . .

. . .

. . .

. . .

. . .

Alloy 5154

O

 

 

all

 

all

 

205

285

75

. . .

. . .

. . .

H112

 

 

all

 

all

 

205

. . .

75

. . .

. . .

. . .

Alloy 5454

O

 

 

. . .

130.00^L

. . .

20 000

215

285

85

. . .

14

12

H111

 

 

. . .

130.00^L

. . .

20 000

230

. . .

130

. . .

12

10

H112

 

 

. . .

130.00^L

. . .

20 000

215

. . .

85

. . .

12

10

F^D

 

 

all

 

all

 

. . .

. . .

. . .

. . .

. . .

. . .

Alloy 5456

O

 

 

. . .

130.00^L

. . .

20 000

285

365

130

. . .

14

12

H111

 

 

. . .

130.00^L

. . .

20 000

290

. . .

180

. . .

12

10

H112

 

 

. . .

130.00^L

. . .

20 000

285

. . .

130

. . .

12

10

F^D

 

 

all

 

all

 

. . .

. . .

. . .

. . .

. . .

. . .

Alloy 6005

T1

 

 

. . .

12.50

all

 

170

. . .

105

. . .

16

14

T5

 

. . .

3.20

all

 

260

. . .

240

. . .

8

. . .

 

 

 3.20

25.00

all

 

260

. . .

240

. . .

10

9

Alloy 6005A

T1

 

 

. . .

6.30

all

 

170

. . .

100

. . .

15

. . .

T5

 

 

. . .

6.30

all

 

260

. . .

215

. . .

7

. . .

 

 

 

 6.30

25.00

all

 

260

. . .

215

. . .

9

8

T61

 

 

. . .

6.30

all

 

260

. . .

240

. . .

8

. . .

 

 

 

6.30

25.00

all

 

260

. . .

240

. . .

10

9

Alloy 6013

T6

 

 

5.00

12.50

all

 

340

. . .

315

. . .

8

. . .

 

 

 

12.50

20.00

all

 

340

. . .

315

. . .

. . .

7

 

 

 

20.00

50.00

all

 

340

. . .

310

. . .

. . .

7

T6511

 

 

5.00

12.50

all

 

340

. . .

315

. . .

8

. . .

 

 

 

12.50

20.00

all

 

340

. . .

315

. . .

. . .

7

 

 

 

20.00

50.00

all

 

340

. . .

310

. . .

. . .

7

Alloy 6020

T6511

 

 

80.00

160.00

all

 

260

. . .

240

. . .

. . .

9

Alloy 6041

T6^M

 

 

10.00

50.00

all

 

310

. . .

275

. . .

10

9

T6511^M

 

 

10.00

50.00

all

 

310

. . .

275

. . .

10

9

Alloy 6042

T5

 

 

10.00

12.50

all

 

260

. . .

240

. . .

10

. . .

 

 

 

12.50

50.00

all

 

290

. . .

240

. . .

. . .

9

T551

 

 

10.00

12.50

all

 

260

. . .

240

. . .

10

. . .

 

 

 

12.50

50.00

all

 

290

. . .

240

. . .

. . .

9

Alloy 6060

T51

 

 

. . .

3.20

all

 

150

. . .

110

. . .

8

. . .

T61

 

 

. . .

3.20

all

 

205

. . .

170

. . .

8

. . .

 

 

 

3.20

25.00

all

 

205

. . .

170

. . .

10

9

Alloy 6061

O

 

 

all

 

all

 

. . .

150

. . .

110

16

14

T1

 

 

. . .

16.00

all

 

180

. . .

95

. . .

16

14

T4

 

 

 

all

 

180

. . .

110

. . .

16

14

T4510^E

 

all

 

 

 

 

 

 

 

 

 

T4511^E

 

 

 

 

 

 

 

 

 

 

 

T42^F

 

 

all

 

all

 

180

. . .

85

. . .

16

14

T51

 

 

. . .

16.00

all

 

240

. . .

205

. . .

8

7

T6, T62^F

. . .

6.30

all

 

260

. . .

240

. . .

8

. . .

T6510^E

 6.30

. . .

all

 

260

. . .

240

. . .

10

9

T6511^E

 

 

 

 

 

 

 

 

 

 

F^D

 

 

all

 

all

 

. . .

. . .

. . .

. . .

. . .

. . .

Alloy 6063

O

 

 

all

 

all

 

. . .

130

. . .

. . .

18

16

T1

 

 

. . .

12.50

all

. . .

115

. . .

60

. . .

12

10

 

 

 

12.50

25.00

all

. . .

110

. . .

55

. . .

. . .

10

T4,T42^F

 

 

. . .

12.50

all

 

130

. . .

70

. . .

14

12

 

 

 

12.50

25.00

all

 

125

. . .

60

. . .

. . .

12

T5

 

 

. . .

12.50

all

 

150

. . .

110

. . .

8

7

 

 

 

12.50

25.00

all

 

145

. . .

105

. . .

. . .

7

T52

 

 

. . .

25.00

all

 

150

205

110

170

8

7

T54

 

 

. . .

3.20

all

 

225

. . .

205

. . .

8

. . .

 

 

 

3.20

12.50

all

 

225

. . .

205

. . .

10

. . .

T6, T62^K,F

 

 

. . .

3.20

all

 

205

. . .

170

. . .

8

. . .

 

 

 

 3.20

25.00

all

 

205

. . .

170

. . .

10

9

T65

 

 

. . .

5.00

all

 

250

. . .

230

. . .

7

. . .

Alloy 6064

T6

 

 

5.00

80.00

all

 

290

. . .

260

. . .

10

9

T6511

 

 

5.00

80.00

all

 

290

. . .

260

. . .

10

9

Alloy 6066

O

 

 

all

 

all

 

. . .

200

. . .

125

16

14

T4

 

 

 

all

 

275

. . .

170

. . .

14

12

T4510^E

 

all

 

 

 

 

 

 

 

 

 

T4511^E

 

 

 

 

 

 

 

 

 

 

 

T42^F

 

 

all

 

all

 

275

. . .

165

. . .

14

12

T6

 

 

 

all

 

345

. . .

310

. . .

8

7

T6510^E

 

all

 

 

 

 

 

 

 

 

 

T6511^E

 

 

 

 

 

 

 

 

 

 

 

T62^F

 

 

all

 

all

 

345

. . .

290

. . .

8

7

Alloy 6070

T6, T62^F

 

 

. . .

80.00

. . .

20 000

330

. . .

310

. . .

6

5

Alloy 6082

T6

 

 

5.00

20.00

all

 

310

...

260

...

6

8

T6511

 

 

20.00

150.00

all

 

310

...

260

...

 

8

 

 

 

150.00

200.00

all

 

280

...

240

...

 

8

Alloy 6105

T1

 

 

. . .

12.5

all

 

170

. . .

105

. . .

16

14

T5

 

 

. . .

3.20

all

 

250

. . .

240

. . .

8

. . .

 

 

 

 3.20

25.00

all

 

250

. . .

240

. . .

10

9

Alloy 6162

T5,

 

. . .

25.00

all

 

255

. . .

235.

. . .

7

6

T5510^E

 

 

 

 

 

 

 

 

 

 

 

T5511^E

 

 

 

 

 

 

 

 

 

 

 

T6,

 

. . .

6.30

all

 

260

. . .

240

. . .

8

. . .

T6510^E

 

 6.30

12.50

all

 

260

. . .

240

. . .

10

9

T6511^E

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

Alloy 6262

T6

 

 

 

 

 

 

 

 

 

 

 

T6510^E

 

all

 

all

 

260

. . .

240

. . .

10

9

T6511^E

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

 

Alloy 6351

T1

 

 

. . .

12.50

. . .

13 000

180

. . .

90

. . .

15

13

T11

 

 

. . .

20.00

all

 

180

. . .

110

. . .

16

14

T4

 

 

. . .

20.00

all

 

220

. . .

130

. . .

16

14

T5

 

 

. . .

6.30

all

 

260

. . .

240

. . .

8

. . .

 

 

 

 6.30

25.00

all

 

260

. . .

240

. . .

10

9

T51

 

 

 3.20

25.00

. . .

13 000

250

. . .

230

. . .

10

7

T54

 

 

. . .

12.50

. . .

13 000

205

. . .

140

. . .

10

9

T6

 

 

. . .

3.20

all

 

290

. . .

255

. . .

8

. . .

 

 

 

 3.20

20.00

all

 

290

. . .

255

. . .

10

9

Alloy 6360

T5

 

 

. . .

6.30

all

 

150

. . .

110

. . .

8

. . .

T6

 

 

. . .

3.20

all

 

205

. . .

170

. . .

8

. . .

 

 

 

3.20

6.30

all

 

205

. . .

170

. . .

10

. . .

Alloy 6463

T1

 

 

. . .

12.50

. . .

13 000

115

. . .

60

. . .

12

10

T5

 

 

. . .

12.50

. . .

13 000

150

. . .

110

. . .

8

7

T6,T62^F

 

 

. . .

3.20

. . .

13 000

205

. . .

170

. . .

8

. . .

 

 

 

 3.20

12.50

. . .

13 000

205

. . .

170

. . .

10

9

Alloy 6560

T5

 

 

2.50

3.20

all

 

150

...

110

...

8

...

T6

 

 

2.50

3.20

all

 

205

...

170

...

8

...

Alloy 7005

T53

 

 

 

20.00

all

 

345

. . .

305

. . .

10

9

Alloy 7116

T5

 

 

 3.20

12.50

all

 

330

. . .

290

. . .

8

7

Alloy 7129

T5, T6

 

 

. . .

12.50

all

 

380

. . .

340

. . .

9

8

Alloy 7075

O

 

 

all

 

all

 

. . .

275

. . .

165

10

9

T6

. . .

6.30

all

 

540

. . .

485

. . .

7

. . .

T62^F

 6.30

12.50

all

 

560

. . .

505

. . .

7

6

T6510^E

 12.50

70.00

all

 

560

. . .

495

. . .

. . .

6

T6511^E

 70.00

110.00

. . .

13 000

560

. . .

490

. . .

. . .

6

 

 

 70.00

110.00^L

13 000

20 000

540

. . .

485

. . .

. . .

5

 

 

110.00

130.00^L

. . .

20 000

540

. . .

470

. . .

. . .

5

T73

 1.60

6.30

. . .

13 000

470

. . .

400

. . .

7

. . .

T73510^E

 6.30

35.00

. . .

16 000

485

. . .

420

. . .

8

7

T73511^E

 35.00

70.00

. . .

16 000

475

. . .

405

. . .

. . .

7

 

 

 70.00

110.00^L

. . .

13 000

470

. . .

395

. . .

. . .

6

 

 

 70.00

110.00^L

13 000

20 000

450

. . .

380

. . .

. . .

6

 

 

. . .

1.25

all

 

500

. . .

435

. . .

7

. . .

 

 

 1.25

3.20

all

 

510

. . .

440

. . .

7

. . .

T76

 3.20

6.30

. . .

13 000

510

. . .

440

. . .

7

. . .

T76510^E

 6.30

12.50

. . .

13 000

515

. . .

450

. . .

7

6

T76511^E

 12.50

25.00

. . .

13 000

515

. . .

450

. . .

. . .

6

 

 

 25.00

50.00

. . .

13 000

515

. . .

450

. . .

. . .

6

 

 

 50.00

75.00

. . .

13 000

510

. . .

440

. . .

. . .

6

 

 

 75.00

100.00

. . .

13 000

510

. . .

435

. . .

. . .

6

F^D

 

 

all

 

all

 

. . .

. . .

. . .

. . .

. . .

. . .

Alloy 7178

O

 

 

all

 

. . .

20 000

. . .

275

. . .

165

10

9

 

 

. . .

1.60

all

 

565

. . .

525

. . .

. . .

. . .

 

 

 1.60

6.30

. . .

13 000

580

. . .

525

. . .

5

. . .

T6

 6.30

35.00

. . .

16 000

600

. . .

540

. . .

5

4

T6510^E

 35.00

60.00

. . .

16 000

595

. . .

530

. . .

. . .

4

T6511^E

 35.00

60.00

16 000

20 000

580

. . .

515

. . .

. . .

4

 

 

 60.00

80.00

. . .

20 000

565

. . .

490

. . .

. . .

4

 

 

. . .

1.60

all

 

545

. . .

505

. . .

. . .

. . .

 

 

 1.60

6.30

. . .

13 000

565

. . .

510

. . .

5

. . .

 

 

 6.30

35.00

. . .

16 000

595

. . .

530

. . .

5

4

T62^F

 

 35.00

60.00

. . .

16 000

595

. . .

530

. . .

. . .

4

 

 

 35.00

60.00

16 000

20 000

580

. . .

515

. . .

. . .

4

 

 

 60.00

80.00

. . .

20 000

565

. . .

490

. . .

. . .

4

T76

 3.20

6.30

. . .

13 000

525

. . .

455

. . .

7

. . .

T76510^E

 6.30

12.50

. . .

13 000

530

. . .

460

. . .

7

6

T76511^E

 12.50

25.00

. . .

13 000

530

. . .

460

. . .

. . .

6

F^D

 

 

all

 

all

 

. . .

. . .

. . .

. . .

. . .

. . .

^A The basis for establishment of tensile property limits is shown in Annex A1.^B To determine conformance to this specification, each value shall be rounded to the nearest 1 MPa for strength and the nearest 0.5 % for elongation, in accordance with the rounding-off method of Practice E29.^C Elongations in 50 mm apply for shapes tested in full section and for sheet-type specimens machined from material up through 12.5 mm in thickness having parallel surfaces. Elongations in 5× diameter (5.65


), where D and A are diameter and cross-sectional area of the specimen respectively, apply to round test specimens machined from thicknesses over 6.30. See 8.1.1 and 8.1.2 for conditions under which measurements are not required.^D No mechanical properties are specified or guaranteed.^E For stress-relieved tempers (T3510, T3511, T4510, T4511, T5510, T5511, T6510, T6511, T73510, T73511, T76510, T76511, T8510, T8511), characteristics and properties offer than those specified may differ somewhat from the corresponding characteristics and properties of material in the basic tempers.^F Material in the T42 and T62 tempers is not available from the material producers.^G Minimum elongation for tube, 10 % in 50 mm and 9 % in 5× diameter.^H Minimum yield strength for tube, 330 MPa.^I Minimum yield strength for tube 315 MPa.^J Yield strength is not applicable to tube.^K Only in tube form.^L Properties not applicable to extruded tube over 70 mm wall thickness.^M Tentative—properties subject to revision.Note 1—Throughout this specification the use of the term alloy in the general sense includes aluminum as well as aluminum alloy.Note 2—For rolled or cold-finished bars and rods refer to Specification B211M, for drawn seamless tube used in pressure applications, Specification B210M, for structural pipe and tube, Specification B429/B429M, and for seamless pipe and tube used in pressure applications, Specification B241/B241M. Note 3— Pipe and tube products listed in this specification are intended for general purpose applications. This specification may not address the manufacturing processes, integrity testing, and verification required for fluid-carrying applications involving pressure. See Specifications B210M and/or B241/B241M, as appropriate, for seamless pipe and tube used in fluid-carrying applications involving pressure. See Specification B234, as appropriate, for use in surface condensers, evaporators, and heat exchangers.

1.2 Alloy and temper designations are in accordance with ANSI H35.1/H35.1M. The equivalent Unified Numbering System alloy designations are those of Table 1 preceded by A9, for example, A91100 for Aluminum 1100 in accordance with Practice E527.

1.3 For acceptance criteria for inclusion of new aluminum and aluminum alloys in this specification, see Annex A2.

1.4 This specification is the metric counterpart of Specification B221.

1.5 The values stated in SI are to be regarded as standard. No other units of measurement are included in this specification.