ASTM B338-13

Заменен
Standard Specification for Seamless and Welded Titanium and Titanium Alloy Tubes for Condensers and Heat Exchangers — 8 стр.
Реферат

This specification covers 28 grades of seamless and welded titanium alloy tubes for surface condensers, evaporators, and heat exchangers. Seamless tube shall be made from hollow billet by any cold reducing or cold drawing process that will yield a product meeting the requirements prescribed. Welded tube shall be made from flat-rolled product by an automatic arc-welding process. The welded tube shall be sufficiently cold worked to final size in order to transform the cast weld microstructure into a typical equiaxed microstructure in the weld upon subsequent heat treatment. The titanium shall conform to the chemical requirements prescribed. The room temperature tensile properties of the tube in the condition normally supplied shall conform to the requirements prescribed. Tubing shall withstand, without cracking, flattening under a load applied gradually at room temperature until the distance between the load platens is not more than the required height. Welded tube shall be subjected to a reverse flattening test in accordance with supplement II of test methods and definitions A 370. Welded tubing shall be tested using both a non-destructive electromagnetic test and an ultrasonic test method. Seamless and welded/cold worked tubing shall be tested using an ultrasonic test method. Welded tubing shall be tested with a hydrostatic or pneumatic test method. Seamless tubing shall be tested with an electromagnetic or hydrostatic or pneumatic test method.

Область применения

1.1 This specification2 covers the requirements for 28 grades of titanium and titanium alloy tubing intended for surface condensers, evaporators, and heat exchangers, as follows:

1.1.1 Grade 1—Unalloyed titanium,

1.1.2 Grade 2—Unalloyed titanium,

1.1.2.1 Grade 2H—Unalloyed titanium (Grade 2 with 58 ksi minimum UTS),

1.1.3 Grade 3—Unalloyed titanium,

1.1.4 Grade 7—Unalloyed titanium plus 0.12 to 0.25 % palladium,

1.1.4.1 Grade 7H—Unalloyed titanium plus 0.12 to 0.25 % palladium (Grade 7 with 58 ksi minimum UTS),

1.1.5 Grade 9—Titanium alloy (3 % aluminum, 2.5 % vanadium),

1.1.6 Grade 11—Unalloyed titanium plus 0.12 to 0.25 % palladium,

1.1.7 Grade 12—Titanium alloy (0.3 % molybdenum, 0.8 % nickel),

1.1.8 Grade 13—Titanium alloy (0.5 % nickel, 0.05 % ruthenium),

1.1.9 Grade 14—Titanium alloy (0.5 % nickel, 0.05 % ruthenium),

1.1.10 Grade 15—Titanium alloy (0.5 % nickel, 0.05 % ruthenium),

1.1.11 Grade 16—Unalloyed titanium plus 0.04 to 0.08 % palladium,

1.1.11.1 Grade 16H—Unalloyed titanium plus 0.04 to 0.08 % palladium (Grade 16 with 58 ksi minimum UTS),

1.1.12 Grade 17—Unalloyed titanium plus 0.04 to 0.08 % palladium,

1.1.13 Grade 18—Titanium alloy (3 % aluminum, 2.5 % vanadium) plus 0.04 to 0.08 % palladium,

1.1.14 Grade 26—Unalloyed titanium plus 0.08 to 0.14 % ruthenium,

1.1.14.1 Grade 26H—Unalloyed titanium plus 0.08 to 0.14 % ruthenium (Grade 26 with 58 ksi minimum UTS),

1.1.15 Grade 27—Unalloyed titanium plus 0.08 to 0.14 % ruthenium,

1.1.16 Grade 28—Titanium alloy (3 % aluminum, 2.5 % vanadium) plus 0.08 to 0.14 % ruthenium,

1.1.17 Grade 30—Titanium alloy (0.3 % cobalt, 0.05 % palladium),

1.1.18 Grade 31—Titanium alloy (0.3 % cobalt, 0.05 % palladium),

1.1.19 Grade 33—Titanium alloy (0.4 % nickel, 0.015 % palladium, 0.025 % ruthenium, 0.15 % chromium),

1.1.20 Grade 34—Titanium alloy (0.4 % nickel, 0.015 % palladium, 0.025 % ruthenium, 0.15 % chromium),

1.1.21 Grade 35—Titanium alloy (4.5 % aluminum, 2 % molybdenum, 1.6 % vanadium, 0.5 % iron, 0.3 % silicon),

1.1.22 Grade 36—Titanium alloy (45 % niobium),

1.1.23 Grade 37—Titanium alloy (1.5 % aluminum),

1.1.24 Grade 38—Titanium alloy (4 % aluminum, 2.5 % vanadium, 1.5 % iron), and

1.1.25 Grade 39—Titanium alloy (0.25 % iron, 0.4 % silicon).

Note 1H grade material is identical to the corresponding numeric grade (that is, Grade 2H = Grade 2) except for the higher guaranteed minimum UTS, and may always be certified as meeting the requirements of its corresponding numeric grade. Grades 2H, 7H, 16H, and 26H are intended primarily for pressure vessel use.

The H grades were added in response to a user association request based on its study of over 5200 commercial Grade 2, 7, 16, and 26 test reports, where over 99 % met the 58 ksi minimum UTS.

1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.

ICS
23.040.15 Non-ferrous metal pipes / Трубы из цветных металлов
Сборник ASTM
02.04 Nonferrous Metals – Nickel, Titanium, Lead, Tin, Zinc, Zirconium, Precious, Reactive, Refractory Metals and Alloys: Materials for Thermostats, Electrical Heating and Resistance Contact, and Connectors / Цветные металлы - Никель, Кобальт, Свинец, Олово, Цинк, Кадмий, Драгоценные металлы, химически активные металлы, Тугоплавкие металлы и сплавы, Материалы для Термостатов, Электронагревательных приборов, Контактов, Соединительные устройств
Тематика
Other Nonferrous Metals