ASTM B359/B359M-12

Заменен
Standard Specification for Copper and Copper-Alloy Seamless Condenser and Heat Exchanger Tubes With Integral Fins — 11 стр.
Реферат

This specification establishes the requirements for seamless copper and copper alloy tubing on which the external or internal surface, or both, has been modified by a coldforming process to produce an integral enhanced surface for improved heat transfer. The tubes are typically used in surface condensers, evaporators, and heat exchangers. The seamless copper and copper alloy tubing shall have the internal or external surface, or both, modified by a cold forming process to produce an integral enhanced surface for improved heat transfer. The tube, after enhancing, shall be supplied in the annealed (O61) or as-fabricated temper. The enhanced sections of tubes in the as-fabricated temper are in the cold-worked condition produced by the fabricating operation. The unenhanced sections of tubes in the asfabricated temper are in the temper of the tube prior to enhancing, annealed (O61), or light drawn (H55), and suitable for rolling-in operations. Samples of annealed-temper (O61) tubes selected for test shall be subjected to microscopical examination and shall show uniform and complete recrystallation. Grain size and mechanical properties such as tensile strength and yield strength of the alloys shall be determined. Expansion and flattening tests shall be done to the alloys for performance evaluation. Non-destructive tests such as eddy-current test, hydrostatic test, and pneumatic test shall be done as well.

Область применения

1.1 This specification establishes the requirements for seamless copper and copper alloy tubing on which the external or internal surface, or both, has been modified by a cold-forming process to produce an integral enhanced surface for improved heat transfer.

1.2 UnitsThe values stated in either in-pound units or SI units are to be regarded separately as the standard. Within the text, the SI units are shown in brackets. The values stated in each system are not exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems could result in nonconformance with the specification.

1.3 The tubes are typically used in surface condensers, evaporators, and heat exchangers.

1.4 The product shall be produced of the following coppers or copper alloys, as specified in the ordering information.

Copper or Copper Alloy
UNS No.
Type of Metal
C10100Oxygen-free electronic C10200Oxygen-free without residual deoxidants C10300Oxygen-free, extra low phosphorus C10800Oxygen-free, low phosphorus C12000DLP Phosphorized, low residual phosphorus
(See Note 1) C12200DHP, Phosphorized, high residual phosphorus
(See Note 1) C14200DPA Phosphorized arsenical
(See Note 1) C19200Phosphorized, 1 % iron C23000Red Brass C44300Admiralty Metal Types B, C44400C, and C44550D C60800Aluminum Bronze C68700Aluminum Brass Type B C7040095-5 Copper-Nickel C7060090-10 Copper-Nickel C7062090-10 Copper-Nickel (Modified for Welding) C7100080-20 Copper-Nickel Type A C7150070-30 Copper-Nickel C7152070-30 Copper-Nickel (Modified for Welding) C72200Copper-Nickel

Note 1—Designations listed in Classification B224.

1.5 The following safety hazard caveat pertains only to the test methods described in this specification. This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

1.6 Product produced in accordance with the Supplementary Requirements section for military applications shall be produced only to the inch-pound system of this specification.

ICS
23.040.15 Non-ferrous metal pipes / Трубы из цветных металлов