Причина отмены This test method described the conditions and equipment for measuring the impedance of anodic coatings on aluminum. Such measurements have been used to evaluate the quality of seal of an anodic coating. The test method did not prescribe the procedure for producing the anodic coating, nor the postanodizing treatment usually described as “sealing.”

Formerly under the jurisdiction of Committee B08 on Metallic and Inorganic Coatings, this guide was withdrawn in June 2023 and replaced by Test Method D8370 for Field Measurement of Electrochemical Impedance on Coatings and Linings.1

Реферат

This test method describes the conditions and equipment for measuring the impedance of anodic coatings on aluminum. Such measurements have been used to evaluate the quality of seal of an anodic coating. The test method does not prescribe the procedure for producing the anodic coating, nor the postanodizing treatment usually described as "sealing." This test method is applicable to the rapid, nondestructive testing of anodic coatings. The interpretation of results and correlation of data with service experience and other tests are not within the scope of this test method. The impedance of anodic coatings is defined in terms of resistance and capacitive reactance. The apparatus to be used shall have the characteristics specified for the following: (1) impedance bridge range, frequency, accuracy, and voltage, (2) cell components such as glass tube, rubber gasket or seal, rubber stopper, and platinum or Type 300 stainless steel counter electrode, (3) wire leads, (4) support strand, (5) glass or stainless steel tank, and (6) container for cell standardization. The conditions for the test specimen and electrolyte, and the procedure of measurement, cell standardization, and temperature correction are detailed. The test cell construction and test set-up are illustrated.

Область применения

1.1 This test method describes the conditions and equipment for measuring the impedance of anodic coatings on aluminum. Such measurements have been used to evaluate the quality of seal of an anodic coating. The test method does not prescribe the procedure for producing the anodic coating, nor the postanodizing treatment usually described as “sealing.”

1.2 This test method is applicable to the rapid, nondestructive testing of anodic coatings. The interpretation of results and correlation of data with service experience and other tests are not within the scope of this test method.

1.3 The values stated in SI units are to be regarded as the standard. The values given in parentheses are for information only.

1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.

1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.