This specification deals with the standard requirements for nickel-chromium-iron-molybdenum-copper alloys (UNS N06007, N06975, N06985, and N06030) in the form of plate, sheet, and strip for use in general corrosive services. These materials shall undergo hot or cold rolling, solution annealing, and descaling. The plates shall have sheared or cut machined, abrasive cut, powder cut, or inert arc cut edges while the sheet and strip shall have sheared or slit edges. Heat and product analysis shall be performed to determine the chemical composition of the specimens which shall conform to the specified nickel, chromium, iron, molybdenum, copper, manganese, cobalt, carbon, tungsten, silicon, phosphorus, sulfur, columbium, tantalum, and titanium limits. The materials shall also conform to the mechanical property requirements for tensile strength, yield strength, elongation, and Rockwell hardness.
Область применения1.1 The specification2 covers plate, sheet, and strip of nickel-chromium-iron-molybdenum-copper alloys (UNS N06007, N06975, N06985, and N06030)* as shown in Table 1, for use in general corrosive service.
TABLE 1 Chemical RequirementsElement
Composition Limits, %
Alloy N06007
Alloy N06975
Alloy N06985
Alloy N06030
Nickel
remainderA
47.0 to 52.0
remainderA
remainderA
Chromium
21.0 to 23.5
23.0 to 26.0
21.0 to 23.5
28.0 to 31.5
Iron
18.0 to 21.0
remainderA
18.0 to 21.0
13.0 to 17.0
Molybdenum
5.5 to 7.5
5.0 to 7.0
6.0 to 8.0
4.0 to 6.0
Copper
1.5 to 2.5
0.70 to 1.20
1.5 to 2.5
1.0 to 2.4
Manganese
1.0 to 2.0
1.0 max
1.0 max
1.5 max
Cobalt, max
2.5
...
5.0
5.0
Carbon, max
0.05
0.03
0.015
0.03
Tungsten
1.0 max
...
1.5 max
1.5 to 4.0
Silicon, max
1.0
1.0
1.0
0.8
Phosphorus, max
0.04
0.03
0.04
0.04
Sulfur, max
0.03
0.03
0.03
0.02
Columbium + tantalum
1.75 to 2.50
...
0.50 max
0.30 to 1.50
Titanium
...
0.70–1.50
...
...
A The composition of the remainder element shall be determined arithmetically by difference.1.2 The following products are covered under this specification:
1.2.1 Sheet and Strip—Hot or cold rolled, solution annealed, and descaled unless solution anneal is performed in an atmosphere yielding a bright finish.
1.2.2 Plate—Hot or cold rolled, solution annealed, and descaled.
1.3 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to become familiar with all hazards including those identified in the appropriate Material Safety Data Sheet (MSDS) for this product/material as provided by the manufacturer, to establish appropriate safety and health practices, and determine the applicability of regulatory limitations prior to use.