ASTM B86-09a

Заменен
Standard Specification for Zinc and Zinc-Aluminum (ZA) Alloy Foundry and Die Castings — 8 стр.
Реферат

This specification covers commercial zinc, zinc-aluminum castings and continuous cast bar stock. Seven alloy compositions are specified and designated: Alloy 3; Alloy 7; Alloy 5; Alloy 2; ZA-8; ZA-12; ZA-27. The metal used in the manufacture of die castings shall be zinc alloy of a specified chemical composition conforming to the requirements specified. Impact test and tension test shall be made to conform to the specified requirements.

Область применения

1.1 This specification covers commercial zinc, zinc-aluminum castings and continuous cast bar stock, as designated and specified in Table 1. Seven alloy compositions are specified and designated as follows:

CommonTraditional ASTM AUNS Alloy 3Zamak 3AG 40A BZ33520 Alloy 7Zamak 7AG 40BZ33523 Alloy 5Zamak 5AC 41A BZ35531 Alloy 2Zamak 2AC 43AZ35541 ZA-8ZA-8...Z35636 ZA-12 ZA-12...Z35631 ZA-27 ZA-27...Z35841 _________

A See Table 1, Footnote C.

B SAE Specification, Nos. 903 and 925 conform to the requirements for alloys AG40A and AC41A, respectively.



1.2 Zinc Alloys Z33520, Z33523, Z35531, and Z35541 are used primarily in the manufacture of pressure die castings. Zinc-Aluminum Alloys Z35636, Z35631, and Z35841 are used in the manufacture of both foundry and pressure die castings. These alloys are also fabricated into continuous cast bar stock used for prototyping and screw machine stock.

1.3 The values stated in inch-pound units are to be regarded as standard.

1.4 Systems of nomenclature used to designate zinc and zinc-aluminum (ZA) alloys used for casting are described in Appendix X1.

1.5 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to become familiar with all hazards including those identified in the appropriate Material Safety Data Sheet (MSDS) for this product/material as provided by the manufacturer, to establish appropriate safety and health practices, and determine the applicability of regulatory limitations prior to use.

TABLE 1 Chemical Requirements

ElementAlloy 3A,B,C,D
Zamak 3
(AG40A)
Z33520Alloy 7A ,B,C,D
Zamak 7
(AG40B)
Z33523Alloy 5A,B,C,D
Zamak 5
(AC41A)
Z35531Alloy 2A,C,,D
Zamak
(AC43A)
Z355412ZA-8A,C,E
ZA-8

Z35636ZA-12A,C ,E
ZA-12

Z35631ZA-2A,C,E
ZA-27

Z35841 Aluminum3.7-4.33.5-4.33.7-4.3 3.7-4.38.0-8.810.5-11.525.0-28.0 Magnesium0.02-0.06F 0.005-0.0200.02-0.06F0.02-0.06 0.01-0.030.01-0.030.01-0.02 Copper 0.1 maxG0.25 max0.7-1.22.6-3.30.8-1.30.5-1.2 2.0-2.5 Iron, max0.050.0750.050.050.0750.0750.075 Lead, max0.0050.0030.005 0.0050.0060.0060.006 Cadmium, max0.0040.0020.004 0.0040.0060.0060.006 Tin, max0.0020.0010.002 0.0020.0030.0030.003 Nickel . . .0.005-0.020. . .. . .. . .. . .. . . ZincHremainder remainderremainderremainder remainderremainderremainder

A For purposes of acceptance and rejection, the observed value or calculated value obtained from analysis should be rounded to the nearest unit in the last right-hand place of figures, used in expressing the specified limit, in accordance with the rounding procedure prescribed in Practice E 29.

B Zinc alloy castings may contain nickel, chromium, silicon, and manganese in amounts of 0.02, 0.02, 0.035, and 0.06 %, respectively. No harmful effects have ever been noted due to the presence of these elements in these concentrations and, therefore, analyses are not required for these elements, with the exception of nickel analysis for Z33522.

C ASTM alloy designations were established in accordance with Practice B 275. The UNS designations were established in accordance with Practice E 527. The last digit of a UNS number differentiates between alloys of similar composition. The UNS designations for ingot and casting versions of an alloy were not assigned in the same sequence for all alloys.

D When this material is required to conform to ISO 301, the chemical limits for thallium and indium each shall not exceed 0.001 %.

E Zinc-aluminum ingot for foundry and pressure die casting may contain chrome, manganese, or nickel in amounts of up to 0.01 % each or 0.03 % total. No harmful effects have ever been noted due to the presence of these elements in up to these concentrations and, therefore, analyses are not required for these elements.

F Magnesium may be as low as 0.015 % provided that the lead, cadmium, and tin do not exceed 0.003, 0.003, and 0.001 %, respectively.

G For the majority of commercial applications, a copper content up to 0.7 % will not adversely affect the serviceability of die castings and should not serve as a basis for rejection, unless otherwise specified in the contract or purchase order between the producer and user, such as to meet the requirements of ISO 15201.

H Determined arithmetically by difference.

Сборник ASTM
02.04 Nonferrous Metals – Nickel, Titanium, Lead, Tin, Zinc, Zirconium, Precious, Reactive, Refractory Metals and Alloys: Materials for Thermostats, Electrical Heating and Resistance Contact, and Connectors / Цветные металлы - Никель, Кобальт, Свинец, Олово, Цинк, Кадмий, Драгоценные металлы, химически активные металлы, Тугоплавкие металлы и сплавы, Материалы для Термостатов, Электронагревательных приборов, Контактов, Соединительные устройств
Тематика
Other Nonferrous Metals