This specification covers the standard for aluminum-alloy centrifugal castings. This specification does not cover aluminum-alloy centrifugal castings used in aerospace applications. The castings shall be in accordance to the prescribed chemical composition. Chemical composition shall be determined by analyzing samples at the time the castings are poured, or samples taken from castings or tension test specimens. Unless otherwise stated, the tensile strength, yield strength and elongation of test specimens cut from casting shall be in accordance with the standards prescribed herein. If the specimens fail to conform to tension requirements, test bars representative of the castings may be retested in accordance with the replacement tests and retest provisions.
Область применения1.1 This specification covers aluminum-alloy centrifugal castings designated as shown in Table 1.
(A) When single units are shown, these indicate the maximum amounts permitted.(B) Analysis shall be made for the elements for which limits are shown in this table.(C) The following applies to all specified limits in this table: For purposes of determining conformance to these limits, an observed value or a calculated value obtained from analysis shall be rounded to the nearest unit in the last right-hand place of figures used in expressing the specified limit in accordance with the rounding method of Practice E29.(D) ASTM alloy designations are defined in ANSI H35.1/H35.1 (M).(E) Others includes listed elements for which no specific limit is shown as well as unlisted metallic elements. The producer may analyze samples for trace elements not specified in the specification. However, such analysis is not required and may not cover all metallic Others elements. Should any analysis by the producer or the purchaser establish that an Others element exceeds the limit of Each or that the aggregate of several Others elements exceeds the limit of Total, the material shall be considered nonconforming.(F) 2Other Elements—Total shall be the sum of unspecified metallic elements 0.010 % or more, rounded to the second decimal before determining the sum.(G) If the iron content exceeds 0.45 %, manganese content shall not be less than one half of the iron.1.2 This specification is not intended for aluminum-alloy centrifugal castings used in aerospace applications.
1.3 Alloy and temper designations are in accordance with ANSI H35.1/H35.1 (M). The equivalent unified numbering system alloy designations are in accordance with Practice E527.
1.4 Unless the order specifies the “M” specification designation, the material shall be furnished to the inch-pound units.
1.5 For acceptance criteria for inclusion of new aluminum and aluminum alloys and their properties in this specification, see Annex A1 and Annex A2.
1.6 Units—The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.
1.7 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitation prior to use.