Значение и использование

This test method indicates the ability of a refractory product to withstand the stress generated by sudden changes in temperature.

Because the recommended furnace temperature of this cycling test is 1200°C (2190°F), this test method may not indicate the ability of a refractory product to withstand cycling at higher or lower temperatures, especially if the existing morphology of the refractory product changes.

This test method is useful for research and development, as well as for comparing refractory products. The precision should be considered when using this test for specification purposes.

Ruggedness tests found the following variables to be rugged:

temperature +5°C hot spacing ½ to ³/₄in. (12.77 to 19 mm) cold spacing ½ to ³/₄ in. (12.77 to 19 mm) center vs. end gripping of the bars
hot hold time 10 to 15 min cold hold time 10 to 15 min operator air speed 0 to 2 mi/h (0 to 3.2 km/h) initially cold or heated samples
last in, first out (LIFO); or first in, first out (FIFO)
removal from the furnace
sawed or original surface as tensile face during MOR testing bar thickness 0.96 to 1.04 in. (24.5 to 26.4 mm)

Область применения

1.1 This test method is used for determining the strength loss or reduction in continuity, or both, of prism-shaped specimens which are cut from refractory brick or shapes and subjected to thermal cycling.

1.2 The strength loss is measured by the difference in modulus of rupture (MOR) between uncycled specimens and the specimens subjected to thermal cycling.

1.3 The reduction in structural continuity is estimated by the difference in sonic velocity before and after thermal cycling.

1.4 The values stated in inch-pound units are to be regarded as the standard. The values stated in parentheses are for information only.

1.5This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.