ASTM C651-13
Заменен
Standard Test Method for Flexural Strength of Manufactured Carbon and Graphite Articles Using Four-Point Loading at Room Temperature
— 4 стр.
Описание
Ссылки
Версии
Ссылочные документы
ASTM E691-14
Заменен
Standard Practice for Conducting an Interlaboratory Study to Determine the Precision of a Test Method
— 21 стр.
ASTM C709-09
Отменен
Standard Terminology Relating to Manufactured Carbon and Graphite (Withdrawn 2017)
— 4 стр.
ASTM C1161-13
Заменен
Standard Test Method for Flexural Strength of Advanced Ceramics at Ambient Temperature
— 19 стр.
ASTM E177-14
Заменен
Standard Practice for Use of the Terms Precision and Bias in ASTM Test Methods
— 9 стр.
ASTM C78-09
Заменен
Standard Test Method for Flexural Strength of Concrete (Using Simple Beam with Third-Point Loading)
— 4 стр.
ASTM E4-14
Заменен
Standard Practices for Force Verification of Testing Machines
— 10 стр.
ASTM C651-15
Заменен
Standard Test Method for Flexural Strength of Manufactured Carbon and Graphite Articles Using Four-Point Loading at Room Temperature
— 4 стр.
ASTM C651-11
Заменен
Standard Test Method for Flexural Strength of Manufactured Carbon and Graphite Articles Using Four-Point Loading at Room Temperature
— 4 стр.
На этот документ ссылаются
ASTM C651-11
Заменен
Standard Test Method for Flexural Strength of Manufactured Carbon and Graphite Articles Using Four-Point Loading at Room Temperature
— 4 стр.
ASTM C781-08
Заменен
Standard Practice for Testing Graphite and Boronated Graphite Materials for High-Temperature Gas-Cooled Nuclear Reactor Components
— 10 стр.
ASTM C1025-91(2010)e1
Заменен
Standard Test Method for Modulus of Rupture in Bending of Electrode Graphite
— 3 стр.
ASTM C651-15
Заменен
Standard Test Method for Flexural Strength of Manufactured Carbon and Graphite Articles Using Four-Point Loading at Room Temperature
— 4 стр.
ASTM D7775-11e1
Заменен
Standard Guide for Measurements on Small Graphite Specimens
— 8 стр.