This test method covered the measurement of the molding index of thermosetting plastics ranging in flow from soft to stiff by selection of appropriate molding pressures within the range from 4.1 to 31.9 MPa.

Formerly under the jurisdiction of Committee D20 on Plastics, this test method was withdrawn in August 2008 in accordance with section 10.5.3.1 of the Regulations Governing ASTM Technical Committees, which requires that standards shall be updated by the end of the eighth year since the last approval date.

This test method provides a guide for evaluating the moldability of thermosetting molding powders. This test method does not necessarily denote that the molding behavior of different materials will be alike and trials may be necessary to establish the appropriate molding index for each material in question.

The sensitivity of this test diminishes when the molding pressure is decreased below 764 psi (5.3 MPa), so pressures lower than this are not ordinarily recommended. This is due to the friction of moving parts and the insensitivity of the pressure switch actuating the timer at these low pressures.

1.1 This test method covers the measurement of the molding index (plasticity) of thermosetting plastics ranging in flow from soft to stiff by selection of appropriate molding pressures within the range from 530 to 5300 psi (3.7 to 36.5 MPa).

1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.

1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

Note 1—There is no ISO standard equivalent to this test method.