This test method covers procedures for evaluation of stress corrosion cracking (SCC) resistance by the breaking load test method, a concept which uses residual strength as the measure of damage evolution (in this case environmentally assisted cracking).

Formerly under the jurisdiction of Committee G01 on Corrosion of Metals, this test method was withdrawn in January 2005 for failure to update within the 8-year period.

1.1 This test method covers procedures for evaluation of stress corrosion cracking (SCC) resistance by the breaking load test method, a concept which uses residual strength as the measure of damage evolution (in this case environmentally assisted cracking).

1.2 This test method covers specimen type and replication , test environment, stress levels, exposure periods, final strength determination, and statistical analysis of the raw residual strength data.

1.3 The test method was developed for use with heat-treatable aluminum alloys. that is, 2XXX alloys and 7XXX with 1.2 to 3 percent Cu, and test specimens oriented in the short-transverse direction relative to grain structure (1,2). However, the residual strength measurements and the statistics used to analyze the data are not specific to heat-treatable aluminum alloys and can be used for other specimen orientations and different types of materials.

1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.