4.1 The 3.5 % NaCl alternate immersion procedure is a general, all-purpose procedure that produces valid comparisons for most metals, particularly when specimens are exposed at high levels of applied stress or stress intensity.

4.2 While the alternate immersion test is an accelerated test and is considered to be representative of certain natural conditions, it is not intended to predict performance in specialized chemical environments in which a different mode of cracking may be operative. For example, it does not predict the performance of aluminum alloys in highly acidic environments such as heated inhibited red fuming nitric acid (IRFNA). For such cases, the results of the alternate immersion test are of doubtful significance until a relationship has been established between it and anticipated service environments.

4.3 While this practice is applicable in some degree to all metals, it is not equally discriminative of all alloys, even within the same metal system. Consequently, information should be established to allow comparisons of performances of the alloy of interest in the alternate immersion test and in natural environments.

Note 2: The alternate immersion concept can be useful for exposure of corrosion specimens in other solutions because the procedure and apparatus provide a controlled set of conditions. Details of this are beyond the scope of this practice.

1.1 This practice covers procedures for making alternate immersion stress corrosion tests in 3.5 % sodium chloride (NaCl) (Note 1). It is primarily for tests of aluminum alloys (Test Method G47) and ferrous alloys, but may be used for other metals exhibiting susceptibility to chloride ions. It sets forth the environmental conditions of the test and the means for controlling them.

Note 1: Alternate immersion stress corrosion exposures are sometimes made in substitute ocean water (without heavy metals) prepared in accordance with Practice D1141. The general requirements of this present practice are also applicable to such exposures except that the reagents used, the solution concentration, and the solution pH should be as specified in Practice D1141.

1.2 This practice can be used for both stressed and unstressed corrosion specimens. Historically, it has been used for stress-corrosion cracking testing, but is often used for other forms of corrosion, such as uniform, pitting, intergranular, and galvanic.

1.3 This practice is intended for alloy development and for applications where the alternate immersion test is to serve as a control test on the quality of successive lots of the same material. Therefore, strict test conditions are stipulated for maximum assurance that variations in results are attributable to variations in the material being tested.

1.4 The values stated in SI units are to be regarded as standard. The values given in parentheses after SI units are provided for information only and are not considered standard.

1.5 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.

1.6 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.