1.1 This European Standard specifies requirernents for continuously
electrolytic zinc-nicke1 coated cold rolled flat products
of low carbon steels suitable for cold forming according to table
1 and table 2 in rolled widths 2 600 mrn and thicknesses from
0,35 mm up to and including 3 mrn, delivered as strip (in coil
form), sheet, slit strip or cut lengths obtained from slit strip
or sheet. The coating is composed of Zn with a Ni-content of
10,5 % to 13 %.
1.2 This European Standard may also be applied to the coating
requirements of continuously electrolytic zinc-nicke1 coated
cold rolled flat products of
a) steels according to EN 10139 (cold rolled strip in rolled
widths < 600 mm),
b) other types of low carbon steel for cold forming,
C) steels normally characterized by minimum yield strength
values in addition to formability parameters, e. g.
- steels with high yield strength and improved formability
according to EN 10268 or other microalloyed steels,
- rephosphorized steels and bake-hardening steels,
- general purpose structural steels.
1.3 By special agreement at the time of ordering this European
Standard may be applied to the coating requirements of
continuously electrolytic zinc-nicke1 coated hot-rolled steel
flat products ( e . g . according to EN 10025, EN 10111, EN 10149-1
to EN 10149-3 etc. ) .
1.4 The coating masses, surface qualities and surface finishes
are given in 5.9, 5.11 and table 3. As the mass of the zincnicke1
coating applied is relatively small, the material is not
intended to withstand outside exposure without further chemical
treatment and painting.
1.5 This European Standard is not applicable to
- hot-dip zinc coated steel strip and sheet (see EN 10142 and
EN lOl47),
- electrolytically zinc coated cold rolled flat products (see
- continuously hot-dip aluminium-silicon (AS) coated steel
strip and sheet (see EN 10154).
- continuously organic coated steel flat p (...abbreviated)
Die vorliegende Norm EN 10271 enthält die Anforderungen an kontinuierlich elektrolytisch Zink-Nickel-veredelte kaltgewalzte Flacherzeugnisse aus weichen Stählen zum Kaltumformen nach Tabelle 1 und Tabelle 2 in gewalzten Breiten 600 mm und mit einer Dicke von 0,35 mm bis 3 mm, die als Band (in Rollen), Blech, längsgeteiltes Band oder daraus abgelängte Stäbe geliefert werden. Der Überzug besteht aus Zink mit einem Nickelgehalt von 12 % 1,5 %. Diese Norm kann auch auf kontinuierlich elektrolytisch Zink-Nickel-veredelte kaltgewalzte Flacherzeugnisse aus a) Stählen nach EN 10139 (Kaltband in Walzbreiten < 600 mm); b) anderen weichen Stählen zum Kaltumformen; und c) Stählen, die üblicherweise in Ergänzung zu den Anforderungen an die Unformbarkeit durch Mindestwerte für die Streckengrenzen gekennzeichnet sind, angewendet werden, z.B. -Stähle mit hoher Streckgrenze und verbesserter Unformbarkeit nach prEN 10268 oder andere mikrolegierte Stähle, -phosphorlegierte Stähle und bake-hardening-Stähle