This European Standard specifies the conditions for the determination of constant-amplitude of load or strain
in uniaxial tension/tension or in uniaxial tension/compression cyclic fatigue properties of ceramic matrix
composite materials (CMCs) with fibre reinforcement for temperature up to 2 000 °C under vacuum or a gas
atmosphere which is inert to the material under test.
NOTE Test environments are specified which are intended to prevent the material under test from chemically
reacting with them.
This European Standard applies to all ceramic matrix composites with fibre reinforcement, unidirectional (1D),
bi-directional (2D), and tri-directional (xD, where 2 < x <= 3).
Diese Europäische Norm legt für faserverstärkte Verbundwerkstoffe mit keramischer Matrix (CMC) die Bedingungen zur Bestimmung der Dauerschwingeigenschaften bei Temperaturen bis zu 2 000 °C im Vakuum oder in einer gegenüber dem zu prüfenden Werkstoff inerten Gasatmosphäre fest, wenn eine einachsige Beanspruchung innerhalb des Zugschwell- (Zug/Zug) oder des Wechselbereichs (Zug/Druck) so aufgebracht wird, dass eine Last oder Dehnung mit konstanter Amplitude erreicht wird. Der Zweck dieser Norm besteht darin, das Verhalten der CMC zu bestimmen, wenn sie gleichzeitig einer mechanischen Dauerschwingbeanspruchung und einer Oxidation ausgesetzt werden. Im Gegensatz zu den Prüfungen zur Bestimmung der Dauerschwingeigenschaften bei hoher Temperatur in inerter Atmosphäre treten bei den Prüfungen, die bei hoher Temperatur und in oxidierender Umgebung durchgeführt werden, Werkstoffschädigungen verstärkt dadurch auf, dass neben der rein mechanischen Ermüdung auch chemische Einflüsse durch die Oxidation des Werkstoffs wirksam werden.