This part of EN 843 specifies methods for determining the elastic moduli, specifically Young s modulus, shear
modulus and Poisson s ratio, of advanced monolithic technical ceramics at room temperature. This European
Standard prescribes four alternative methods for determining some or all of these three parameters:
A The determination of Young s modulus by static flexure of a thin beam in three- or four-point flexure.
B The determination of Young s modulus by forced longitudinal resonance, or Young s modulus, shear
modulus and Poisson s ratio by forced flexural and torsional resonance, of a thin beam.
C The determination of Young s modulus, shear modulus and Poisson s ratio from the time-of-flight of an
ultrasonic pulse.
D The determination of Young s modulus from the fundamental natural frequency of a struck bar (impulse
excitation method).
All the test methods assume the use of homogeneous test pieces of linear elastic materials.
NOTE 1 Not all ceramic materials are equally and linearly elastic in tension and compression, such as some porous
materials and some piezoelectric materials.
With the exception of Method C, the test assumes that the test piece has isotropic elastic properties. Method C
may be used to determine the degree of anisotropy by testing in different orientations.
NOTE 2 An ultrasonic method for dealing with anisotropic materials (ceramic matrix composites) can be found in
ENV 14186 [1]. An alternative to Method D for isotropic materials using disc test pieces is given in
Annex A.
NOTE 3 At high porosity levels all of the methods except Method C may become inappropriate. The methods are only
suitable for a maximum grain size (see EN 623-3), excluding deliberately added whiskers, of less than 10 % of the minimum
dimension of the test piece.
NOTE 4 The different methods given in this European Standard can produce slightly different results on the same
material owing to difference (...abbreviated)
Dieser Teil von EN 843 legt Verfahren zur Bestimmung der elastischen Moduln, speziell des Elastizitätsmoduls, des Schubmoduls und der Poissonzahl von keramischen Hochleistungswerkstoffen bei Raumtemperatur fest. Die Norm legt vier alternativ anwendbare Verfahren für die Bestimmung eines oder aller dieser drei Parameter fest. Alle Prüfverfahren setzen aus homogenen linearelastischen Werkstoffen gefertigte Probekörper voraus. Mit Ausnahme von Verfahren C wird bei der Prüfung vorausgesetzt, dass der Probekörper isotrope elastische Eigenschaften besitzt. Verfahren C kann angewendet werden, um den Grad an Anisotropie in unterschiedlichen Richtungen zu bestimmen. Bei hohen Porositätsgraden können sich alle Verfahren als ungeeignet erweisen. Die maximale Korngröße (siehe EN 623-3), ausgenommen absichtlich eingebrachte Whisker, muss 10 % kleiner als das kleinste Maß des Probekörpers sein.