This International Standard specifies two procedures for the determination of the melt mass-flow rate (MFR)
and the melt volume-flow rate (MVR) of thermoplastic materials under specified conditions of temperature and
load. Procedure A is a mass-measurement method. Procedure B is a displacement-measurement method.
Normally, the test conditions for measurement of melt flow rate are specified in the material standard with a
reference to this International Standard. The test conditions normally used for thermoplastics are listed in
Annexes A and B.
The MVR will be found particularly useful when comparing materials of different filler content and when
comparing filled with unfilled thermoplastics. The MFR can be determined from MVR measurements provided
the melt density at the test temperature and pressure is known.
These methods are in principle also applicable to thermoplastics for which the rheological behaviour is
affected during the measurement by phenomena such as hydrolysis, condensation or crosslinking, but only if
the effect is limited in extent and only if the repeatability and reproducibility are within an acceptable range.
For materials which show significantly affected rheological behaviour during testing, these methods are not
appropriate. In such cases, the use of the viscosity number in dilute solution, determined in accordance with
the relevant part of ISO 1628, is recommended for characterization purposes.
NOTE The rates of shear in these methods are much smaller than those used under normal conditions of processing,
and therefore data obtained by these methods for various thermoplastics may not always correlate with their behaviour
during processing. Both methods are used primarily in quality control.
Dieses Dokument legt zwei Verfahren für die Bestimmung der Schmelze-Massefließrate (MFR) und der Schmelze-Volumenfließrate (MVR) von thermoplastischen Materialien unter festgelegten Bedingungen für Temperatur und Belastung fest. Verfahren A dient zum Bestimmen der Masse. Verfahren B ist ein Messverfahren für die Weglänge. Üblicherweise sind die Prüfbedingungen für die Messung der Schmelze-Massefließrate oder Schmelze-Volumenfließrate in der Werkstoffnorm mit einem Verweis auf dieses Dokument festgelegt. Die üblicherweise für Thermoplaste angewendeten Bedingungen sind in den Anhängen A und B aufgelistet. Die MVR erweist sich beim Vergleichen von Werkstoffen mit unterschiedlichen Füllstoffanteilen und beim Vergleichen von gefüllten und ungefüllten Thermoplasten als besonders nützlich. Die MFR kann, falls die Dichte der Schmelze bei der Prüftemperatur und dem Prüfdruck bekannt ist, aus MVR-Messungen bestimmt werden.