1.1 This International Standard specifies a method for determining the flexural properties of fibrereinforced
plastic composites under three-point (Method A) and four-point (Method B) loading. Standard
test specimens are defined but parameters included for alternative specimen sizes for use where
appropriate. A range of test speeds is included.
1.2 The method is not suitable for the determination of design parameters, but may be used for
screening materials, or as a quality-control test.
NOTE – For example, the flexural modulus is only an appropriate value of the tensile Young s
modulus of elasticity as the test is not for the additional deflection due to the shear stress which
leads to a lower value of the flexural modulus but uses test span/specimen thickness ratios that
minimise this effect. Differences between tensile and flexural properties are also caused by the
material structure/lay-up.
1.3 The method is suitable for fibre-reinforced thermoplastic and thermosetting plastic composites.
Unreinforced and particle-filled plastics and plastics reinforced with short (i.e. less than 1 mm length)
fibres are covered by ISO 178.
1.4 The method is performed using specimens which may be moulded to the chosen dimensions,
machined from the central portion of the standard multi-purpose test specimen (see ISO 3167) or
machined from semi-finished or finished products such as mouldings or laminates.
1.5 The method specifies preferred dimensions for the specimen. Tests which are carried out on
specimens of other dimensions, or on specimens which are prepared under different conditions, may
produce results which are not comparable. Other factors, such as the speed of testing and the
conditioning of the specimens can influence the results. For materials which are not homogeneous
through the section, or above the linear-elastic response region, the result applies only to the thickness
and structure tested. Co (...abbreviated)
Diese Norm legt ein Verfahren zur Bestimmung der Biegeeigenschaften von faserverstärkten Kunststoffen nach dem Drei- und dem Vierpunkt-Verfahren (Verfahren A bzw. B) fest. Es werden Norm-Probekörper festgelegt, jedoch sind die Parameter für andere Probekörpergrößen, falls angemessen, enthalten. Für die Prüfgeschwindigkeiten wird ein Bereich angegeben. Das Verfahren wird für die Untersuchung des Biegeverhaltens der Probekörper und für die Bestimmung der Biegefestigkeit, des Biegemoduls und anderer Gesichtspunkte der Spannungs-Dehnungs-Beziehung unter den definierten Bedingungen verwendet. Es wendet einen frei unterstützten Balken an, der nach dem Drei- oder dem Vierpunkt-Verfahren belastet wird. Das Verfahren ist für Probekörper geeignet, die entweder direkt in den angegebenen Maßen geformt werden, aus dem Mittelteil eines Norm-Vielzweckprobekörpers (siehe ISO 3167) oder aus halbfertigen Produkten, z. B. aus Formteilen, Schichtstoffen und extrudierten oder gegossenen Tafeln, ausgearbeitet werden.