This document specifies an ultrasonic method to determine the components of the elasticity tensor of ceramic matrix composite materials at room temperature. Young’s moduli shear moduli and Poisson coefficients, can be determined from the components of the elasticity tensor.
This document applies to ceramic matrix composites with a continuous fibre reinforcement: unidirectional (1D), bidirectional (2D), and tridirectional (×D, with 2 < × = 3) which have at least orthotropic symmetry, and whose material symmetry axes are known.
This method is applicable only when the ultrasonic wavelength used is larger than the thickness of the representative elementary volume, thus imposing an upper limit to the frequency range of the transducers used.
Dieses Dokument legt ein Ultraschallverfahren fest, mit dem die Komponenten des Elastizitätstensors von keramischen Matrixverbunden bei Raumtemperatur zu bestimmen sind. Aus den Komponenten des Elastizitätstensors können E-Modul, Schermodul und Querkontraktionszahl bestimmt werden.
Dieses Dokument gilt für keramische Matrixverbunde mit unidirektionaler (1D), bidirektionaler (2D) sowie dreidirektionaler (×D, mit 2 kleiner × kleiner gleich 3) Endlosfaserverstärkung, die mindestens eine orthotrope Symmetrie haben und deren Werkstoff-Symmetrieachsen bekannt sind.
Dieses Verfahren ist nur anwendbar, wenn Ultraschall angewendet wird, dessen Wellenlänge größer ist als die Dicke des repräsentativen Volumenelements, wodurch eine obere Grenze für den Frequenzbereich der verwendeten Prüfköpfe festgelegt wird.